| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | MD：3.00mm | ASTMD955 | 1.8到2.2 | % |
| Water absorption rate | Equilibrium,23°C,69%RH | ASTMD570 | 0.22 | % |
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238 | 27 | g/10min |
| Density/specific gravity | | ASTMD792 | 1.41 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength | Yield | ASTMD638 | 60.8 | Mpa |
| compressive strength | 1%Strain | ASTMD695 | 31.4 | Mpa |
| compressive strength | 10%Strain | ASTMD695 | 108 | Mpa |
| elongation | Break | ASTMD638 | 45 | % |
| Bending modulus | | ASTMD790 | 2550 | Mpa |
| bending strength | | ASTMD790 | 93.2 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ASTMD648 | 158 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed | ASTMD648 | 110 | °C |
| Linear coefficient of thermal expansion | MD | ASTMD696 | 8.5E-05 | cm/cm/°C |
| Melting temperature | | DSC | 165 | °C |
| Vicat softening temperature | | ASTMD1525 | 162 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity 3 | | ASTMD257 | 1E+16 | ohms |
| Volume resistivity 3 | 23°C | ASTMD257 | 1E+14 | ohms·cm |
| Dielectric strength | 2.00mm | ASTMD149 | 24 | KV/mm |
| Dielectric constant | 50Hz | IEC60250 | 3.80 | |
| Dielectric constant | 1kHz | IEC60250 | 3.80 | |
| Dielectric constant | 1MHz | IEC60250 | 3.80 | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | 53 | J/m |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M-Scale | ASTMD785 | 80 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.