| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Density/specific gravity | | ISO1183 | 1.41 | g/cm³ |
| Melt mass flow rate | 190°C/2.16kg | ISO1133 | 27 | g/10min |
| Melt volume flow rate | 190°C/2.16kg | ISO1133 | 23.0 | cm3/10min |
| Water absorption rate | 23°C,24hr | ISO62 | 0.50 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | | ISO527-2 | 63.0 | Mpa |
| Nominal tensile fracture strain | | ISO527-2 | 30 | % |
| Bending modulus | | ISO178 | 2550 | Mpa |
| Bending stress | | ISO178 | 88.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 100 | °C |
| Linear coefficient of thermal expansion | MD:23to55°C | 内部方法 | 1.1E-04 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD:23to55°C | 内部方法 | 1.1E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Dielectric strength | 3.00mm | IEC60243-1 | 19 | KV/mm |
| Leakage Trace Index | | IEC60112 | >600 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 5.3 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M-Sale | ISO2039-2 | 80 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | HB | |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| ColourNumber | | | CF2001 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.