Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Density/specific gravity | | ASTMD792 | 1.17 | g/cm³ |
| Melt mass flow rate | 230°C/3.8kg | ASTMD1238 | 2.7 | g/10min |
| Shrinkage rate | MD | ASTMD955 | 0.40to0.80 | % |
| Water absorption rate | 24hr | ASTMD570 | 0.40 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strength | Yield | ASTMD638 | 48.1 | Mpa |
| elongation | Yield | ASTMD638 | 85 | % |
| Bending modulus | | ASTMD790 | 2140 | Mpa |
| bending strength | Yield | ASTMD790 | 86.3 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ASTMD648 | 84.0 | °C |
| Vicat softening temperature | | ASTMD15252 | 98.0 | °C |
| Linear coefficient of thermal expansion | MD | ASTMD696 | 7E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume resistivity | | ASTMD257 | >1.0E+15 | ohms·cm |
| Dielectric strength 3 | | ASTMD149 | 15 | KV/mm |
| Dielectric constant | 60Hz | ASTMD150 | 3.10 | |
| Dissipation factor | 60Hz | ASTMD150 | 0.040 | |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | | ISO179/1eA | 4.0 | kJ/m² |
| Impact strength of simply supported beam without notch | | ISO179/1eU | 40 | kJ/m² |
| NotchedIzodImpact | Area | ASTMD256 | 3.70 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | M-Scale | ASTMD785 | 61 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Refractive index | | ASTMD542 | 1.490 | |
| transmissivity | 3200µm | ASTMD1003 | 90.0 | % |
| Haze | 3200µm | ASTMD1003 | <1.0 | % |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | HB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.