PA66 Vydyne® 49H NT ASCEND USA
112
- Unit Price:
- $4027 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 33MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:smooth surface High impact High toughness Low temperature toughness High temperature resistan Chemical resistance Oil resistant Solvent resistant Easy to form
- Application Areas:Connector Automotive components
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Across Flow : 2.00 mm | ISO 294-4 | 1.6 | % |
| 流量 : 2.00 mm | ISO 294-4 | 1.8 | % | |
| Water absorption rate | 24 hr, 23°C | ISO 62 | 1.3 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 2.3 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO 527-2 | 3040 | Mpa | |
| Tensile stress | Yield | ISO 527-2 | 70.0 | Mpa |
| Break | ISO 527-2 | 46.0 | Mpa | |
| Tensile strain | Break | ISO 527-2 | 17 | % |
| Bending modulus | ISO 178 | 2600 | Mpa | |
| Bending stress | ISO 178 | 81.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 202 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 69.0 | °C | |
| Melting temperature | ISO 11357-3 | 260 | °C | |
| Linear coefficient of thermal expansion | Flow : 23 to 55°C, 2.00 mm | ISO 11359-2 | 8.6E-5 | cm/cm/°C |
| Across Flow : 23 to 55°C, 2.00 mm | ISO 11359-2 | 1.2E-4 | cm/cm/°C | |
| RTI Elec | 0.75 mm | UL 746 | 130 | °C |
| 1.5 mm | UL 746 | 130 | °C | |
| 3.0 mm | UL 746 | 130 | °C | |
| RTI Imp | 0.75 mm | UL 746 | 75.0 | °C |
| 1.5 mm | UL 746 | 75.0 | °C | |
| 3.0 mm | UL 746 | 75.0 | °C | |
| RTI | 0.75 mm | UL 746 | 110 | °C |
| 1.5 mm | UL 746 | 110 | °C | |
| 3.0 mm | UL 746 | 110 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | 0.750 mm | IEC 60093 | 1.0E+11 | ohms·cm |
| Dielectric strength | 1.00 mm | ASTM D149 | 14 | KV/mm |
| Arc resistance | 3.00 mm | ASTM D495 | PLC 6 | |
| Leakage Trace Index | 3.00 mm | IEC 60112 | 525 | V |
| High arc combustion index (HAI) | 0.75 mm | UL 746 | PLC 0 | |
| 1.5 mm | UL 746 | PLC 0 | ||
| 3.0 mm | UL 746 | PLC 0 | ||
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 2 | ||
| Hot wire ignition (HWI) | 0.75 mm | UL 746 | PLC 4 | |
| 1.5 mm | UL 746 | PLC 4 | ||
| 3.0 mm | UL 746 | PLC 3 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 80 | °C | ||
| drying time | 4.0 | hr | ||
| Suggested maximum recycled material ratio | 25 | % | ||
| Temperature at the rear of the barrel | 280 到 310 | °C | ||
| Temperature in the middle of the barrel | 280 到 310 | °C | ||
| Temperature at the front of the material cylinder | 280 到 310 | °C | ||
| Spray nozzle temperature | 280 到 310 | °C | ||
| Processing (melt) temperature | 285 到 305 | °C | ||
| Mold temperature | 65 到 95 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179 | 无断裂 | |
| 23°C | ISO 179 | 无断裂 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75 mm | UL 94 | HB | |
| 1.5 mm | UL 94 | HB | ||
| 3.0 mm | UL 94 | HB | ||
| Burning wire flammability index | 0.75 mm | IEC 60695-2-12 | 725 | °C |
| 1.5 mm | IEC 60695-2-12 | 750 | °C | |
| 3.0 mm | IEC 60695-2-12 | 700 | °C | |
| Hot filament ignition temperature | 0.75 mm | IEC 60695-2-13 | 750 | °C |
| 1.5 mm | IEC 60695-2-13 | 775 | °C | |
| 3.0 mm | IEC 60695-2-13 | 725 | °C | |
| Automotive Materials - (thickness d = 1 mm) | FMVSS 302 | + |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.