PA66 Vydyne® R530H BK0201 ASCEND USA

173

Unit Price:
$3538 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
68.5MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:--

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	TD:23°C,2.00mm	ISO294-4	0.90	%
Shrinkage rate	Shrinkage rate	MD:23°C,2.00mm	ISO294-4	0.40	%
Water absorption rate	23°C,24hr	ISO62	0.90	%
Water absorption rate	Water absorption rate	Equilibrium,50%RH	ISO62	1.9	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	23°C	ISO527-2	10000	Mpa
Tensile stress	Break,23°C	ISO527-2	195	Mpa
Tensile strain	Break,23°C	ISO527-2	3.0	%
Bending modulus	23°C	ISO178	9600	Mpa
Bending stress	23°C	ISO178	270	Mpa
Poisson's Ratio	23°C	ISO527	0.40

Thermal performance	Test Condition	Test Method	Test Result	Unit
Linear coefficient of thermal expansion	TD：23to55°C,2.00mm	ISO11359-2	1.1E-04	cm/cm/°C
RTIElec	0.75mm	UL746	140	°C
	RTIElec	1.5mm	UL746	140	°C
	RTIElec	RTIElec	3.0mm	UL746	140	°C
Evolution Calendar intelligent importer	0.75mm	UL746	120	°C
	Evolution Calendar intelligent importer	1.5mm	UL746	120	°C
	Evolution Calendar intelligent importer	Evolution Calendar intelligent importer	3.0mm	UL746	120	°C
RTIStr	0.75mm	UL746	125	°C
	RTIStr	1.5mm	UL746	140	°C
	RTIStr	RTIStr	3.0mm	UL746	140	°C
Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	260	°C
Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	250	°C
Melting temperature		ISO11357-3	260	°C
Linear coefficient of thermal expansion	MD：23to55°C,2.00mm	ISO11359-2	2.2E-05	cm/cm/°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Hot wire ignition (HWI)	3.0mm	UL746	PLC4
VolumeResistivity	3.00mm	IEC60093	1E+13	ohms·cm
Dielectric strength	1.00mm	IEC60243	20	KV/mm
Arc resistance	3.00mm	ASTMD495	PLC6
Leakage Trace Index	3.00mm	IEC60112	250to399	V
High arc combustion index (HAI)	0.75mm	UL746	PLC0
	High arc combustion index (HAI)	1.5mm	UL746	PLC0
	High arc combustion index (HAI)	High arc combustion index (HAI)	3.0mm	UL746	PLC0
High voltage arc tracing rate	HVTR	UL746	PLC1
Hot wire ignition (HWI)	0.75mm	UL746	PLC4
Hot wire ignition (HWI)	Hot wire ignition (HWI)	1.5mm	UL746	PLC3

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO179	65	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO179	75	kJ/m²

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.75mm	UL94	HB
	UL flame retardant rating	1.5mm	UL94	HB
	UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	HB
Burning wire flammability index	0.75mm	IEC60695-2-12	675	°C
	Burning wire flammability index	1.5mm	IEC60695-2-12	675	°C
	Burning wire flammability index	Burning wire flammability index	3.0mm	IEC60695-2-12	675	°C
Hot filament ignition temperature	0.75mm	IEC60695-2-13	700	°C
	Hot filament ignition temperature	1.5mm	IEC60695-2-13	700	°C
	Hot filament ignition temperature	Hot filament ignition temperature	3.0mm	IEC60695-2-13	700	°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.