PA66 Vydyne® R530J NT0724 ASCEND USA

Unit Price:
$4123 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
30MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Enhanced level

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	Across Flow : 23°C, 2.00 mm	ISO 294-4	0.90	%
Shrinkage rate	Shrinkage rate	流量 : 23°C, 2.00 mm	ISO 294-4	0.40	%
Water absorption rate	24 hr, 23°C	ISO 62	0.90	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	1.9	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile stress	Break, 23°C	ISO 527-2	195	Mpa
Tensile strain	Break, 23°C	ISO 527-2	3.0	%
Tensile modulus	23°C	ISO 527-2	10000	Mpa
Bending modulus	23°C	ISO 178	9600	Mpa
Bending stress	23°C	ISO 178	270	Mpa
Poisson's Ratio	23°C	ISO 527	0.40

Thermal performance	Test Condition	Test Method	Test Result	Unit
Linear coefficient of thermal expansion	Flow : 23 to 55°C, 2.00 mm	ISO 11359-2	2.2E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 55°C, 2.00 mm	ISO 11359-2	1.1E-4	cm/cm/°C
Melting temperature		ISO 11357-3	260	°C
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	260	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	250	°C
RTI	0.75 mm	UL 746	115	°C
	RTI	1.5 mm	UL 746	120	°C
	RTI	RTI	3.0 mm	UL 746	120	°C
RTI Imp	0.75 mm	UL 746	85.0	°C
	RTI Imp	1.5 mm	UL 746	85.0	°C
	RTI Imp	RTI Imp	3.0 mm	UL 746	105	°C
RTI Elec	0.75 mm	UL 746	120	°C
	RTI Elec	1.5 mm	UL 746	120	°C
	RTI Elec	RTI Elec	3.0 mm	UL 746	120	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
High arc combustion index (HAI)	0.75 mm	UL 746	PLC 0
	High arc combustion index (HAI)	1.5 mm	UL 746	PLC 0
	High arc combustion index (HAI)	High arc combustion index (HAI)	3.0 mm	UL 746	PLC 0
Arc resistance	3.00 mm	ASTM D495	5.00	sec
Volume resistivity	0.750 mm	IEC 60093	1.0E+13	ohms·cm
Dielectric strength	1.00 mm	IEC 60243	24	KV/mm
Leakage Trace Index	3.00 mm	IEC 60112	600	V
Hot wire ignition (HWI)	0.75 mm	UL 746	PLC 4
	Hot wire ignition (HWI)	1.5 mm	UL 746	PLC 4
	Hot wire ignition (HWI)	Hot wire ignition (HWI)	3.0 mm	UL 746	PLC 4
High Voltage Arc Traceability Rate (HVTR)		UL 746	PLC 1

injection	Test Result	Unit
Suggested maximum recycled material ratio	25	%
drying temperature	80	°C
Processing (melt) temperature	285 到 305	°C
Mold temperature	65 到 95	°C
drying time	4.0	hr
Temperature at the rear of the barrel	280 到 310	°C
Temperature in the middle of the barrel	280 到 310	°C
Temperature at the front of the material cylinder	280 到 310	°C
Spray nozzle temperature	280 到 310	°C

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179	65	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179	75	kJ/m²

flammability	Test Condition	Test Method	Test Result	Unit
Burning rate	2.00 mm, 自动灭火	ISO 3795	0.0	mm/min
UL flame retardant rating	0.75 mm	UL 94	HB
	UL flame retardant rating	1.5 mm	UL 94	HB
	UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.