Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Density/specific gravity | | ASTM D-792 | 无水｜1.59 | |
| Density/specific gravity | | ASTM D-792 | 1.3%水｜- | |
| Density/specific gravity | 23°C | g/cm³ | 1.59 | -- |
| Shrinkage rate | TD:3.00mm3 | % | 0.60到0.90 | -- |
| Shrinkage rate | MD:3.00mm4 | % | 0.20到0.50 | -- |
| Water absorption rate | 23°C,24hr | % | 0.60 | -- |
| Water absorption rate | Saturation,23°C | % | 4.0 | -- |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | -40°C | MPa | 190 | -- |
| Tensile stress | 23°C | MPa | 165 | |
| Tensile stress | 80°C | MPa | 110 | -- |
| Tensile fracture strength | 23℃ | ASTM D-638 | 无水｜1640 | kg/cm2 |
| Tensile fracture strength | 23℃ | ASTM D-638 | 1.3%水｜1350 | kg/cm2 |
| elongation at break | 23℃ | ASTM D-638 | 无水｜5 | % |
| elongation at break | 23℃ | ASTM D-638 | 1.3%水｜5 | % |
| Flexural strength | 23℃ | ASTM D-790 | 无水｜2490 | kg/cm2 |
| Flexural strength | 23℃ | ASTM D-790 | 1.3%水｜2000 | kg/cm2 |
| Flexural modulus | 23℃ | ASTM D-790 | 无水｜93200 | kg/cm2 |
| Flexural modulus | 23℃ | ASTM D-790 | 1.3%水｜65000 | kg/cm2 |
| Tensile strain | Break,-40°C | % | 2.5 | -- |
| Tensile strain | Break,23°C | % | 3.0 | 3.0 |
| Tensile strain | Break,80°C | % | 4.5 | -- |
| Bending modulus | -40°C | MPa | 10200 | -- |
| Bending modulus | 23°C | MPa | 9300 | |
| Bending modulus | 80°C | MPa | 5500 | -- |
| Bending stress | -40°C | MPa | 275 | -- |
| Bending stress | 23°C | MPa | 250 | |
| Bending stress | 80°C | MPa | 150 | -- |
| Taber abraser | 1000Cycles | mg | 26.0 | -- |
| IZOD impact strength | 23℃，Unnotched1/8 | | 无水｜65 | kg.cm/cm |
| IZOD impact strength | 23℃，Unnotched1/8 | | 1.3%水｜70 | kg.cm/cm |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,Unannealed | °C | 251 | -- |
| Melting temperature | | °C | 265 | -- |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 2E-05 | -- |
| Linear coefficient of thermal expansion | | ASTM D-696 | 无水｜2 | 10-5cm/cm.℃ |
| Linear coefficient of thermal expansion | | ASTM D-696 | 1.3%水｜- | |
| heat deflection temperature | 18.6kg/cm2 | ASTM D-648 | 无水｜251 | °C |
| heat deflection temperature | 18.6kg/cm2 | ASTM D-648 | 1.3%水｜- | °C |
| melting point | | 差示扫描测热计DSC法 | 无水｜265 | °C |
| melting point | | 差示扫描测热计DSC法 | 1.3%水｜- | °C |
| UL-94 flame retardant grade | | UL 94 | 无水｜V-0 | |
| UL-94 flame retardant grade | | UL 94 | 1.3%水｜- | |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume resistivity | | ASTM D-257 | 无水｜8×1014 | Ω.cm |
| Volume resistivity | | ASTM D-257 | 1.3%水｜8×1013 | Ω.cm |
| Dielectric strength | 1/8" | ASTM D-149 | 无水｜38 | KV/mm |
| Dielectric strength | 1/8" | ASTM D-149 | 1.3%水｜33 | KV/mm |
| IEC Conductive Track Index | | UL 746 | 无水｜200 | V |
| IEC Conductive Track Index | | UL 746 | 1.3%水｜- | V |
| Loss factor | 106Hz | ASTM D-150 | 无水｜0.003-0.009 | |
| Loss factor | 106Hz | ASTM D-150 | 1.3%水｜- | |
| Arc resistance | 1/8" | ASTM D-495 | 无水｜70-80 | S |
| Arc resistance | 1/8" | ASTM D-495 | 1.3%水｜- | S |
| Volume resistivity | | ohms·cm | 1E+15 | 1E+13 |
| Dielectric strength | | kV/mm | 38 | 33 |
| Dielectric constant 5 | 23°C,1kHz | | 4.00 | -- |
| Dielectric constant 5 | 23°C,1MHz | | 0.0100 | -- |
| Arc resistance 6 | | sec | 70.0 | -- |
| Compared to the anti leakage trace index | CTI | V | 200 | -- |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | -40°C | kJ/m² | 7.0 | -- |
| Charpy Notched Impact Strength | 23°C | kJ/m² | 9.5 | |
| Impact strength of simply supported beam without notch | 23°C | kJ/m² | 65 | |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R-Sale,23°C | | 121 | -- |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Enhanced content | | | 无水｜30 | wt% |
| Enhanced content | | | 1.3%水｜- | wt% |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | 0.40mm | | V-0 | -- |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Water absorption rate | 23℃，24hr | ASTM D-570 | 无水｜0.4 | % |
| Water absorption rate | 23℃，24hr | ASTM D-570 | 1.3%水｜- | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.