Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Shrinkage rate | TD | ISO294-4 | 1.4 | % |
| Shrinkage rate | MD | ISO294-4 | 1.4 | % |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO15512 | 0.30 | % |
| Relative viscosity | | ISO307 | 2.7 | |
| Density/specific gravity | | ISO1183 | 1.14 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | 23°C | ISO527-2 | 3100 | Mpa |
| Tensile stress | Yield,23°C | ISO527-2 | 86.0 | Mpa |
| Nominal tensile fracture strain | 23°C | ISO527-2 | 25 | % |
| Bending modulus | 23°C | ISO178 | 2700 | Mpa |
| Bending stress | 23°C | ISO178 | 100 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 200 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 70.0 | °C |
| Melting temperature | | ISO11357-3 | 260 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC60093 | 1E+12 | ohms |
| Volume resistivity | 2.00mm | IEC60093 | 1E+14 | ohms·cm |
| Dielectric strength | 1.00mm | IEC60243-1 | 32 | KV/mm |
| Leakage Trace Index | 3.00mm | IEC60112 | >600 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Impact strength of cantilever beam gap | 23°C | ISO180 | 4.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Rockwell hardness | R-Sale,23°C | ISO2039-2 | 120 | |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Huangdu Index | | ASTMD1925 | -3.3 | YI |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| UL flame retardant rating | | UL94 | V-2 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.