PA66 Zytel® 70G30HSLR NC010 DUPONT USA
176
Unit Price:$3075 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 22MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability Lubricity Hydrolysis resistance
- Application Areas:Fitness equipment Electrical field Electrical appliances Electronic field Automotive sector
- Color:--
- Grade:Wear resistant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Top out temperature | 210 | °C | ||
| SpecificHeatCapacity of Melt | 2290 | J/kg/°C | ||
| ThermalConductivityofMelt | 0.21 | W/m/K | ||
| MediumDensity | 1.20 | g/cm³ | ||
| Shrinkage rate | TD | ISO294-4 | 1.1 | % |
| MD | ISO294-4 | 0.30 | % | |
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 6.0 | % |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 1.9 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 10000 | Mpa | |
| Tensile stress | Break | ISO527-2 | 200 | Mpa |
| Tensile strain | Break | ISO527-2 | 3.3 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 261 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 253 | °C | |
| Glass transition temperature 2 | ISO11357-2 | 80.0 | °C | |
| Vicat softening temperature | ISO306/B50 | 250 | °C | |
| Melting temperature 2 | ISO11357-3 | 262 | °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO11359-2 | 2.6E-05 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 2.6E-05 | cm/cm/°C | |
| MD：55to160°C | ISO11359-2 | 1.3E-05 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 8E-05 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 7E-05 | cm/cm/°C | |
| TD：55to160°C | ISO11359-2 | 1.3E-04 | cm/cm/°C | |
| TD：EffectiveThermalDiffusivity | ISO11359-2 | 1.1E-07 | m²/s |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 38 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 4.30 | |
| 1MHz | IEC60250 | 4.10 | ||
| Dissipation factor | 100Hz | IEC60250 | 7E-03 | |
| 1MHz | IEC60250 | 0.015 | ||
| Compared to the anti leakage trace index | 3.00mm | UL746 | PLC1 | |
| Leakage Trace Index | IEC60112 | 450 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 70 | kJ/m² |
| 23°C | ISO179/1eU | 80 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning rate 3 | 1.00mm | ISO3795 | 24 | mm/min |
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.75mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| Extreme Oxygen Index | ISO4589-2 | 24 | % | |
| FMVSS flammability | FMVSS302 | SE/B | ||
| atomization | F-value(refraction) | ISO6452 | 95 | % |
| G-value(condensate) | ISO6452 | 3E-04 | g |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 3.20 | µgC/g | |
| Odor | VDA270 | 4.50 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.