PA66 Zytel® 70G25HSLR NC010 DUPONT SHENZHEN
155
Unit Price:$3903 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 115MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High rigidity High temperature resistan
- Application Areas:Electrical applications Bottle cap Automotive Applications
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| 物理性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 收缩率 | 横向流量 | ISO 294-4 | 1.1 | % |
| 流量 | ISO 294-4 | 0.30 | % | |
| 吸水率 | 饱和, 23°C, 2.00 mm | ISO 62 | 6.4 | % |
| 平衡, 23°C, 2.00 mm, 50% RH | ISO 62 | 2.0 | % | |
| Flow Length | 2.00 mm | 350 | mm | |
| 粘数 | ISO 307 | 150 | cm³/g |
| 机械性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 弯曲应力 | ISO 178 | 260 | Mpa | |
| 拉伸应力 | 断裂 | ISO 527-2 | 180 | Mpa |
| 拉伸应变 | 断裂 | ISO 527-2 | 3.0 | % |
| 拉伸模量 | ISO 527-2 | 8500 | Mpa | |
| 弯曲模量 | ISO 178 | 8000 | Mpa |
| 热性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 热变形温度 | 0.45 MPa, 未退火 | ISO 75-2/B | 261 | °C |
| 1.8 MPa, 未退火 | ISO 75-2/A | 252 | °C | |
| 维卡软化温度 | ISO 306/B50 | 257 | °C | |
| 线形热膨胀系数 | 流动 | ISO 11359-2 | 3.3E-5 | cm/cm/°C |
| 横向 | ISO 11359-2 | 1.1E-4 | cm/cm/°C | |
| 玻璃转化温度 3 | ISO 11357-2 | 80.0 | °C | |
| 熔融温度 3 | ISO 11357-3 | 262 | °C |
| 电气性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 相对电容率 | 100 Hz | IEC 62631-2-1 | 3.60 | |
| 漏电起痕指数 | IEC 60112 | 400 | V | |
| 耗散因数 | 100 Hz | IEC 62631-2-1 | 7.0E-3 | |
| 表面电阻率 | IEC 62631-3-2 | -- | ohms | |
| 体积电阻率 | IEC 62631-3-1 | 1.0E+13 | ohms·m |
| 充模分析 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 熔体密度 | 1.15 | g/cm³ | ||
| 顶出温度 | 210 | °C | ||
| Specific Heat Capacity of Melt | 2090 | J/kg/°C | ||
| Thermal Conductivity of Melt | 0.21 | W/m/K | ||
| Odor | VDA 270 | 3.50 |
| 注射 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 干燥温度 | 80 | °C | ||
| 干燥时间 - 热风干燥机 | 2.0 到 4.0 | hr | ||
| 建议的最大水分含量 | 0.20 | % | ||
| 加工（熔体）温度 | 285 到 305 | °C | ||
| Melt Temperature, Optimum | 295 | °C | ||
| 模具温度 | 70 到 120 | °C | ||
| Mold Temperature, Optimum | 100 | °C | ||
| 保压 | 50.0 到 100 | Mpa | ||
| Drying Recommended | yes | |||
| Hold Pressure Time | 3.00 | s/mm | ||
| Maximum Screw Tangential Speed | 12 | m/min |
| 冲击性能 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 简支梁无缺口冲击强度 | -30°C | ISO 179/1eU | 60 | kJ/m² |
| 23°C | ISO 179/1eU | 60 | kJ/m² |
| 硬度 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 球压硬度 | H 961/30 | ISO 2039-1 | 260 | Mpa |
| 可燃性 | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 燃烧速率 | 1.00 mm | ISO 3795 | 26 | mm/min |
| UL 阻燃等级 | 1.5 mm | UL 94, IEC 60695-11-10, -20 | HB | |
| 3.0 mm | UL 94, IEC 60695-11-10, -20 | HB | ||
| FMVSS 可燃性 | FMVSS 302 | B | ||
| 雾化 - G-value (condensate) | ISO 6452 | 5.0E-4 | g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.