PA66 Zytel® FR50 BK505 DUPONT USA
158
- Unit Price:
- $5977 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 46MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Glass fiber reinforced
- Application Areas:Electrical tools Electrical field Electrical appliances Electronic field Automotive sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.60 | ||
| Molding shrinkage rate | ASTM D955 | 0.3~0.7 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Top out temperature | 210 | °C | ||
| Shrinkage rate | TD | ISO294-4 | 0.70 | % |
| MD | ISO294-4 | 0.30 | % | |
| Across Flow | ISO 294-4 | 0.80 | % | |
| 流量 | ISO 294-4 | 0.30 | % | |
| Water absorption rate | 24 hr, 23°C, 2.00 mm | ISO 62 | 0.60 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO 527-2 | 10200 | Mpa | |
| Tensile stress | Break | ISO 527-2 | 170 | Mpa |
| Tensile strain | Break | ISO 527-2 | 2.6 | % |
| elongation at break | ASTM D638/ISO 527 | 2.1 | % | |
| Tensile modulus | ASTM D638/ISO 527 | 10640 | kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 158 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 9410 | kg·cm/cm(J/M)ft·lb/in | |
| Tensile modulus | ISO527-2 | 10600 | Mpa | |
| Tensile stress | Break | ISO527-2 | 158 | Mpa |
| Tensile strain | Break | ISO527-2 | 2.1 | % |
| Bending modulus | ISO178 | 9410 | Mpa | |
| IZOD notch impact strength | ASTM D256/ISO 179 | 8.4 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 7.9 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Combustibility (rate) | UL94 | V-0 | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 242 | ℃（℉） | |
| melting point | 260 | ℃（℉） | ||
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 242 | °C |
| Melting temperature 2 | ISO11357-3 | 260 | °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO11359-2 | 2.1E-05 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 2.5E-05 | cm/cm/°C | |
| MD：55to160°C | ISO11359-2 | 1.2E-05 | cm/cm/°C | |
| TD：-- | ISO11359-2 | 7.9E-05 | cm/cm/°C | |
| TD：-40to23°C | ISO11359-2 | 6.9E-05 | cm/cm/°C | |
| TD：55to160°C | ISO11359-2 | 1.1E-04 | cm/cm/°C | |
| Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 240 | °C |
| Melting temperature 3 | ISO 11357-3 | 262 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 62631-3-2 | -- | ohms | |
| Volume resistivity | IEC 62631-3-1 | > 1.0E+13 | ohms·m | |
| Dielectric strength | 2.00 mm | IEC 60243-1 | 24 | KV/mm |
| Leakage Trace Index | IEC 60112 | 275 | V |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 80 | °C | ||
| Drying time - hot air dryer | 2.0 到 4.0 | hr | ||
| Suggested maximum moisture content | 0.20 | % | ||
| Processing (melt) temperature | 280 到 300 | °C | ||
| Melt Temperature, Optimum | 290 | °C | ||
| Mold temperature | 70 到 120 | °C | ||
| Mold Temperature, Optimum | 100 | °C | ||
| Maintain pressure | 50.0 到 100 | Mpa | ||
| Drying Recommended | yes | |||
| Hold Pressure Time | 3.00 | s/mm | ||
| Maximum Screw Tangential Speed | 12 | m/min |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | ISO 179/1eU | 50 | kJ/m² |
| -30°C | ISO 179/1eU | 50 | kJ/m² | |
| 23°C | ISO 179/1eU | 60 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75 mm | UL 94, IEC 60695-11-10, -20 | V-0 | |
| 1.5 mm | UL 94, IEC 60695-11-10, -20 | V-0 5VA | ||
| Burning rate 3 | 1.00mm | ISO3795 | <100 | mm/min |
| UL flame retardant rating | 0.75mm | UL94 | V-0 | |
| 1.5mm | UL94 | V-05VA | ||
| 0.75mm | IEC60695-11-10,-20 | V-0 | ||
| 1.5mm | IEC60695-11-10,-20 | V-05VA | ||
| Extreme Oxygen Index | ISO4589-2 | 35 | % | |
| FMVSS flammability | FMVSS302 | B |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 4.70 | µgC/g | |
| Odor | VDA270 | 4.50 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.