PA66 Zytel® 70G13L NC010 DUPONT USA
182
Unit Price:$3842 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 50MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced high strength High rigidity High temperature resistan
- Application Areas:Electrical field Electronic field Automotive sector Bottle cap sporting goods Electrical appliances
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.23 | ||
| Molding shrinkage rate | ASTM D955 | 0.7~1.2 | % | |
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 2.2 | % | |
| Shrinkage rate | TD | ISO294-4 | 1.2 | % |
| MD | ISO294-4 | 0.70 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 1.7 | % |
| Saturation,23°C,2.00mm | ISO62 | 7.6 | % | |
| Equilibrium,23°C,2.00mm,50%RH | ISO62 | 2.2 | % | |
| Top out temperature | 210 | °C |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 5500 | Mpa | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 40 | kJ/m² |
| 23°C | ISO179/1eU | 40 | kJ/m² | |
| Unscented Izod impact strength | -30°C | ISO180/1U | 35 | kJ/m² |
| 23°C | ISO180/1U | 40 | kJ/m² | |
| elongation at break | ASTM D638/ISO 527 | 3 | % | |
| Tensile modulus | ASTM D638/ISO 527 | 5500 | kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 120 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 4900 | kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 190 | kg·cm/cm(J/M)ft·lb/in | |
| Tensile stress | Break | ISO527-2 | 120 | Mpa |
| Tensile strain | Break | ISO527-2 | 3.0 | % |
| Bending modulus | ISO178 | 4800 | Mpa | |
| Bending stress | ISO178 | 190 | Mpa | |
| abrasion resistance | ISO4649 | 10.0 | mm³ | |
| Charpy impact strength | ASTM D256/ISO 179 | 5 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 32 | kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 30 | kg·cm/cm(J/M)ft·lb/in | ||
| ASTM D256/ISO 179 | 4.5 (-40℃) | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-- | ISO11359-2 | 9.3E-05 | cm/cm/°C |
| TD：-40to23°C | ISO11359-2 | 7.7E-05 | cm/cm/°C | |
| TD：55to160°C | ISO11359-2 | 1.5E-04 | cm/cm/°C | |
| Combustibility (rate) | UL94 | HB | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 258 | ℃（℉） | |
| ASTM D648/ISO 75 | 238 | ℃（℉） | ||
| melting point | 262 | ℃（℉） | ||
| Linear expansion coefficient | ASTM D696/ISO 11359 | 0.77 | mm/mm.℃ | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 258 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 238 | °C | |
| Glass transition temperature | ISO11357-2 | 80.0 | °C | |
| Vicat softening temperature | ISO306/B50 | 205 | °C | |
| Melting temperature | ISO11357-3 | 262 | °C | |
| Linear coefficient of thermal expansion | MD：-- | ISO11359-2 | 4E-05 | cm/cm/°C |
| MD：-40to23°C | ISO11359-2 | 4.2E-05 | cm/cm/°C | |
| MD：55to160°C | ISO11359-2 | 2.6E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | IEC60243-1 | 25 | KV/mm | |
| Relative permittivity | 100Hz | IEC60250 | 3.90 | |
| 1MHz | IEC60250 | 3.20 | ||
| Dissipation factor | 100Hz | IEC60250 | 0.013 | |
| 1MHz | IEC60250 | 0.015 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning rate | 1.00mm | ISO3795 | 27 | mm/min |
| UL flame retardant rating | 0.71mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 0.71mm | IEC60695-11-10,-20 | HB | ||
| 1.5mm | IEC60695-11-10,-20 | HB | ||
| Extreme Oxygen Index | ISO4589-2 | 24 | % | |
| FMVSS flammability | FMVSS302 | B |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| EmissionofOrganicCompounds | VDA277 | 6.00 | µgC/g |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.