PA66 Zytel® 70G30HSL BK031 DUPONT USA

120

Unit Price:
$3383 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
10MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:Thermal stability
Application Areas:Electrical applications sporting goods
Color:--
Grade:Enhanced level

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	Across Flow	ISO 294-4	1.1	%
Shrinkage rate	Shrinkage rate	流量	ISO 294-4	0.30	%
Water absorption rate	Saturation, 23°C, 2.00 mm	ISO 62	6.9	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 2.00 mm, 50% RH	ISO 62	2.0	%

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile stress	Break	ISO 527-2	195	Mpa
Tensile strain	Break	ISO 527-2	3.5	%
Tensile modulus		ISO 527-2	9800	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	260	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	253	°C
Linear coefficient of thermal expansion	Flow	ISO 11359-2	2.8E-5	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow	ISO 11359-2	9.5E-5	cm/cm/°C
Glass transition temperature 3		ISO 11357-2	80.0	°C
Melting temperature 3		ISO 11357-3	262	°C
Effective Thermal Diffusivity			6.85E-8	m²/s

Electrical performance	Test Condition	Test Method	Test Result	Unit
Dissipation factor	100 Hz	IEC 62631-2-1	0.016
Dissipation factor	Dissipation factor	1 MHz	IEC 62631-2-1	0.016
Compared to the Leakage Tracking Index (CTI)	3.00 mm	UL 746	PLC 0
Leakage Trace Index		IEC 60112	600	V
Surface resistivity		IEC 62631-3-2	--	ohms
Volume resistivity		IEC 62631-3-1	1.0E+11	ohms·m

Filling analysis	Test Method	Test Result	Unit
Melt density		1.21	g/cm³
Specific Heat Capacity of Melt		2290	J/kg/°C
Thermal Conductivity of Melt		0.21	W/m/K
Odor	VDA 270	4.50
Emission of Organic Compounds	VDA 277	6.00	µgC/g

injection	Test Condition	Test Method	Test Result	Unit
drying temperature			80	°C
Drying time - hot air dryer			2.0 到 4.0	hr
Suggested maximum moisture content			0.20	%
Processing (melt) temperature			285 到 305	°C
Melt Temperature, Optimum			295	°C
Mold temperature			70 到 120	°C
Mold Temperature, Optimum			100	°C
Maintain pressure			50.0 到 100	Mpa
Maintain pressure	Maintain pressure	Drying Recommended		yes
Hold Pressure Time			3.00	s/mm
Maximum Screw Tangential Speed			12	m/min

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	60	kJ/m²
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	80	kJ/m²

flammability	Test Condition	Test Method	Test Result	Unit
atomization	F-value (refraction)	ISO 6452	95	%
atomization	atomization	G-value (condensate)	ISO 6452	3.0E-4	g
Burning rate	1.00 mm	ISO 3795	24	mm/min
UL flame retardant rating	0.71 mm	UL 94, IEC 60695-11-10, -20	HB
UL flame retardant rating	UL flame retardant rating	1.5 mm	UL 94, IEC 60695-11-10, -20	HB
FMVSS flammability		FMVSS 302	SE/B
Extreme Oxygen Index		ISO 4589-2	24	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.