PA66 Zytel® 70G43L NC DUPONT SHENZHEN
172
- Unit Price:
- $3667 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced high strength
- Application Areas:Electrical tools Electrical field Electronic field
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Across Flow | ISO 294-4 | 1.0 | % |
| 流量 | ISO 294-4 | 0.30 | % | |
| Water absorption rate | 24 hr, 23°C, 2.00 mm | ISO 62 | 0.90 | % |
| Saturation, 23°C, 2.00 mm | ISO 62 | 4.7 | % | |
| Equilibrium, 23°C, 2.00 mm, 50% RH | ISO 62 | 1.5 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO 527-2 | 14000 | Mpa | |
| Tensile stress | Break | ISO 527-2 | 225 | Mpa |
| Tensile strain | Break | ISO 527-2 | 3.0 | % |
| Tensile creep modulus | 1 hr | ISO 899-1 | -- | Mpa |
| 1000 hr | ISO 899-1 | -- | Mpa | |
| Bending modulus | ISO 178 | 12000 | Mpa | |
| Bending stress | ISO 178 | 340 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 262 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 255 | °C | |
| Glass transition temperature 3 | ISO 11357-2 | 80.0 | °C | |
| Vicat softening temperature | ISO 306/B50 | 255 | °C | |
| Melting temperature 3 | ISO 11357-3 | 262 | °C | |
| Linear coefficient of thermal expansion | Flow | ISO 11359-2 | 1.5E-5 | cm/cm/°C |
| Flow : -40 to 23°C | ISO 11359-2 | 2.0E-5 | cm/cm/°C | |
| Flow : 55 to 160°C | ISO 11359-2 | 9.0E-6 | cm/cm/°C | |
| Across Flow | ISO 11359-2 | 7.9E-5 | cm/cm/°C | |
| Across Flow : -40 to 23°C | ISO 11359-2 | 6.1E-5 | cm/cm/°C | |
| Across Flow : 55 to 160°C | ISO 11359-2 | 1.3E-4 | cm/cm/°C | |
| Effective Thermal Diffusivity | 9.50E-8 | m²/s |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 62631-3-2 | -- | ohms | |
| Volume resistivity | IEC 62631-3-1 | > 1.0E+13 | ohms·m | |
| Dielectric strength | IEC 60243-1 | 27 | KV/mm | |
| Relative permittivity | 1 MHz | IEC 62631-2-1 | 4.10 | |
| 100 Hz | IEC 62631-2-1 | 4.50 | ||
| Dissipation factor | 100 Hz | IEC 62631-2-1 | 0.010 | |
| 1 MHz | IEC 62631-2-1 | 0.015 |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt density | 1.29 | g/cm³ | ||
| Top out temperature | 210 | °C | ||
| Specific Heat Capacity of Melt | 2050 | J/kg/°C | ||
| Thermal Conductivity of Melt | 0.25 | W/m/K |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 80 | °C | ||
| Drying time - hot air dryer | 2.0 到 4.0 | hr | ||
| Suggested maximum moisture content | 0.20 | % | ||
| Processing (melt) temperature | 285 到 305 | °C | ||
| Melt Temperature, Optimum | 295 | °C | ||
| Mold temperature | 70 到 120 | °C | ||
| Mold Temperature, Optimum | 100 | °C | ||
| Maintain pressure | 50.0 到 100 | Mpa | ||
| Drying Recommended | yes | |||
| Hold Pressure Time | 3.00 | s/mm | ||
| Maximum Screw Tangential Speed | 12 | m/min |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 85 | kJ/m² |
| 23°C | ISO 179/1eU | 100 | kJ/m² | |
| Unscented Izod impact strength | -30°C | ISO 180/1U | 110 | kJ/m² |
| 23°C | ISO 180/1U | 110 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M -Sale | ISO 2039-2 | 105 | |
| R -Sale | ISO 2039-2 | 125 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning rate | 1.00 mm | ISO 3795 | 27 | mm/min |
| UL flame retardant rating | 0.71 mm | UL 94, IEC 60695-11-10, -20 | HB | |
| 1.5 mm | UL 94, IEC 60695-11-10, -20 | HB | ||
| Extreme Oxygen Index | ISO 4589-2 | 23 | % | |
| FMVSS flammability | FMVSS 302 | B |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.