Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Density/specific gravity | | ISO1183 | 1.14 | g/cm³ |
| Shrinkage rate | TD | ISO294-4 | 1.4 | % |
| Shrinkage rate | TD:80°C,48hr | ISO294-4 | 0.10 | % |
| Shrinkage rate | MD | ISO294-4 | 1.4 | % |
| Shrinkage rate | MD:80°C,48hr | ISO294-4 | 0.20 | % |
| Water absorption rate | Saturation,23°C,2.00mm | ISO62 | 8.5 | % |
| Water absorption rate | Equilibrium,23°C,2.00mm,50%RH | ISO62 | 2.6 | % |
| Stickiness number | | ISO307 | 140 | cm³/g |
| MediumDensity | | | 0.970 | g/cm³ |
| Top out temperature | | | 190 | °C |
| SpecificHeatCapacity of Melt | | | 2790 | J/kg/°C |
| ThermalConductivityofMelt | | | 0.16 | W/m/K |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | | ISO527-2 | 3100 | Mpa |
| Tensile stress | Yield | ISO527-2 | 82.0 | Mpa |
| Tensile strain | Yield | ISO527-2 | 4.5 | % |
| Nominal tensile fracture strain | | ISO527-2 | 20 | % |
| TensileCreepModule | 1hr | ISO899-1 | -- | Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | -- | Mpa |
| Bending modulus | | ISO178 | 2800 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| EffectiveThermalDiffusivity | | | 5E-08 | m²/s |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 190 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 70.0 | °C |
| Glass transition temperature 2 | | ISO11357-2 | 60.0 | °C |
| Vicat softening temperature | | ISO306/B50 | 240 | °C |
| Melting temperature 2 | | ISO11357-3 | 262 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 1E-04 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Volume resistivity | | IEC60093 | 1E+15 | ohms·cm |
| Dielectric strength | | IEC60243-1 | 32 | KV/mm |
| Relative permittivity | 100Hz | IEC60250 | 3.80 | |
| Relative permittivity | 1MHz | IEC60250 | 3.60 | |
| Dissipation factor | 100Hz | IEC60250 | 0.014 | |
| Dissipation factor | 1MHz | IEC60250 | 0.018 | |
| film | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile strain MD | Yield | ISO527-3 | 4.5 | % |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 4.5 | kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 6.0 | kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 400 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | NoBreak | |
| Impact strength of cantilever beam gap | -40°C | ISO180/1A | 5.5 | kJ/m² |
| Impact strength of cantilever beam gap | -30°C | ISO180/1A | 6.0 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 5.5 | kJ/m² |
| Unscented Izod impact strength | -30°C | ISO180/1U | 300 | kJ/m² |
| Unscented Izod impact strength | 23°C | ISO180/1U | 300 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Extreme Oxygen Index | | ISO4589-2 | 28 | % |
| FMVSS flammability | | FMVSS302 | SE | |
| Fogging-G-value | condensate | ISO6452 | 1E-04 | g |
| UL flame retardant rating | 1.5mm | UL94 | V-2 | |
| UL flame retardant rating | 0.71mm | IEC60695-11-10,-20 | V-2 | |
| UL flame retardant rating | 1.5mm | IEC60695-11-10,-20 | V-2 | |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| EmissionofOrganicCompounds | | VDA277 | 6.50 | µgC/g |
| Odor | | VDA270 | 3.00 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.