PA66 Vydyne® R533H NA ASCEND USA
156
- Unit Price:
- $4014 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 65MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ISO1183 | 1.40 | g/cm³ | |
| Shrinkage rate | TD:23°C,2.00mm | ISO294-4 | 0.90 | % |
| MD:23°C,2.00mm | ISO294-4 | 0.40 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.80 | % |
| 平衡,23°C,50%RH | ISO62 | 1.7 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2 | 10600 | Mpa |
| Tensile stress | 断裂,23°C | ISO527-2 | 205 | Mpa |
| Tensile strain | 断裂,23°C | ISO527-2 | 3.0 | % |
| Bending modulus | 23°C | ISO178 | 10200 | Mpa |
| Bending stress | 23°C | ISO178 | 290 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| RTIStr | 1.5mm | UL746 | 140 | °C |
| 3.0mm | UL746 | 140 | °C | |
| Linear coefficient of thermal expansion | TD：23to55°C,2.00mm | ISO11359-2 | 1.1E-04 | cm/cm/°C |
| RTIElec | 0.75mm | UL746 | 140 | °C |
| 1.5mm | UL746 | 140 | °C | |
| 3.0mm | UL746 | 140 | °C | |
| Hot deformation temperature | 0.45MPa,未退火 | ISO75-2/B | 260 | °C |
| 1.8MPa,未退火 | ISO75-2/A | 250 | °C | |
| Evolution Calendar intelligent importer | 0.75mm | UL746 | 125 | °C |
| 1.5mm | UL746 | 125 | °C | |
| 3.0mm | UL746 | 125 | °C | |
| RTIStr | 0.75mm | UL746 | 140 | °C |
| Melting temperature | ISO11357-3 | 260 | °C | |
| Linear coefficient of thermal expansion | MD：23to55°C,2.00mm | ISO11359-2 | 2.1E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| VolumeResistivity | 0.750mm | IEC60093 | 1E+13 | ohms·cm |
| Dielectric strength | 1.00mm | IEC60243 | 20 | KV/mm |
| Leakage Trace Index | 3.00mm | IEC60112 | 250to399 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 10 | kJ/m² |
| 23°C | ISO179/1eA | 11 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 70 | kJ/m² |
| 23°C | ISO179/1eU | 80 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ISO180 | 10 | kJ/m² |
| 23°C | ISO180 | 12 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot filament ignition temperature | 3.0mm | IEC60695-2-13 | 750 | °C |
| Burning wire flammability index | 0.75mm | IEC60695-2-12 | 725 | °C |
| 1.5mm | IEC60695-2-12 | 700 | °C | |
| 3.0mm | IEC60695-2-12 | 875 | °C | |
| Hot filament ignition temperature | 0.75mm | IEC60695-2-13 | 750 | °C |
| 1.5mm | IEC60695-2-13 | 725 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.