PA66 Ultramid® A3EG10 BASF GERMANY
166
- Unit Price:
- $3077 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 51MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Oil resistant High rigidity
- Application Areas:Electronic insulation Industrial components
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1560 | ||
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 3.7-4.3 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 23℃,50%相对湿度 | % | ISO 62 | |
| melting point | ℃ | ISO 3146 | ||
| Melt volume ratio | cm | ISO 1133 | ||
| Saturation, 23 ℃ | % | 3.5到5.0 | ||
| Balance, 23 ℃, 50% RH | % | 1.2到1.5 | ||
| Shrinkage rate | 23℃ | % | 0.10到0.31 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Break,23℃ | MPa | 144.83到292.41 | |
| Tensile modulus | 23℃ | MPa | 8206.9到28000.0 | |
| Tensile strain | Break,23℃ | % | 1.9到3.1 | |
| Tensile modulus | MPa | ISO 527-2 | ||
| Yield stress | MPa | ISO 527-2 | 230 | |
| Bending modulus | MPa | ISO 178 | ||
| Charpy notch impact strength | KJ/m | ISO 179/1eA | 18 | |
| IZOD notch impact strength | KJ/m | ISO 180/1A | ||
| Tensile modulus | ASTM D638/ISO 527 | 16800 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 15000 | kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 360 | kg·cm/cm(J/M)ft·lb/in | |
| IZOD notch impact strength | ASTM D256/ISO 179 | 13 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | -，0.45Mpa | ℃ | ISO 75-2 | 250 |
| melting point | 260 | ℃（℉） | ||
| Flame retardancy | UL94 | HB | ||
| Hot deformation temperature | -，1.8Mpa | ℃ | ISO 75-2 | 250 |
| Continuous use temperature | °C | 110到220 | ||
| 8.0Mpa, unannealed | °C | 65到220 | ||
| 1.8MPa, unannealed | °C | 230到250 | ||
| transverse | mm/mm/°C | 68.6E-5到127.0E-5 | ||
| flow | mm/mm/°C | 142.2E-5到203.2E-5 | ||
| Melting temperature | °C | 260 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | 23℃ | V/mil | 840 | |
| Volume resistivity | 23℃ | ohms·cm | 1.0E+12到1.0E+14 | |
| ASTM D257/IEC 60093 | 1E 13 | Ω.cm | ||
| Dielectric constant | 1MHz | IEC 60250 | 3.8 | |
| Dielectric loss | 1MHz | IEC 60250 | 0.015 | |
| Volume resistivity | Ω.M | IEC 60093 | ||
| Surface resistivity | Ω | IEC 60093 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 11.143到19.964 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | MPa | 222.76到370.34 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.