PA66 Ultramid® A4H BASF GERMANY
136
- Unit Price:
- $6431 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 43MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Medium viscosity heat-resisting Oil resistant
- Application Areas:wheel Connector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | 23℃ | % | 0.10到0.31 | |
| Saturation, 23 ℃ | % | 3.5到5.0 | ||
| Balance, 23 ℃, 50% RH | % | 1.2到1.5 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus of elasticity | 干/湿 | 3100/1200 | Mpa | |
| Tensile creep modulus | 1000h,湿 | 700 | Mpa | |
| Tensile stress | Break,23℃ | MPa | 144.83到292.41 | |
| Tensile strain | Break,23℃ | % | 1.9到3.1 | |
| Tensile modulus | 23℃ | MPa | 8206.9到28000.0 | |
| elongation | ASTM D638/ISO 527 | 4.2/20 | % | |
| ≤0.5%, +23℃，湿 | 700 | Mpa | ||
| Bending modulus | 干/湿 | 3000 | Mpa | |
| ASTM D790/ISO 178 | 3000 | kg·cm/cm(J/M)ft·lb/in | ||
| Ball pressure hardness | 干/湿 | 160/100 | Mpa | |
| Fracture stress (V=50mm/min) | 干/湿 | 85/50 | Mpa | |
| Kapi notch impact strength | +23℃，干/湿字段1_文本 | 8/30 | KJ/m | |
| Impact and destructive energy | -20℃,干 | 20 | J | |
| +23℃，干/湿 | 50/>140 | J | ||
| Kabi impact strength | +23℃，干/湿 | NB/NB | KJ/m | |
| Yield elongation (V=50mm/min) | 干/湿 | 4.2/20 | % | |
| Tensile yield stress (V=50mm/min) | 干/湿 | 85/50 | Mpa | |
| Izo notch impact strength | -30℃,干 | 7 | KJ/m | |
| +23℃，干/湿 | 5.5/NB | KJ/m | ||
| Elongation at break (V=50mm/min) | 干/湿 | 4.2/20 | % | |
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 4.2/20 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | （23-80）℃，Dry | 7-10 | ||
| 1.8MPa, unannealed | °C | 230到250 | ||
| Maximum operating temperature | >200 | °C | ||
| Temperature index | 在20000h/5000h，后拉伸强度下降50%时 | 118/138 | °C | |
| Hot deformation temperature | ASTM D648/ISO 75 | 220 | ℃（℉） | |
| 0.45MPa负荷，Dry | 220 | °C | ||
| 1.8MPa负荷，Dry | 75 | °C | ||
| Linear expansion coefficient | ASTM D696/ISO 11359 | 7-10 | mm/mm.℃ | |
| Melting temperature | °C | 260 | ||
| Continuous use temperature | °C | 110到220 | ||
| 8.0Mpa, unannealed | °C | 65到220 | ||
| transverse | mm/mm/°C | 68.6E-5到127.0E-5 | ||
| flow | mm/mm/°C | 142.2E-5到203.2E-5 | ||
| Thermal conductivity | Dry | 0.23 | W/(m.K) | |
| Specific heat capacity | Dry | 1.7 | J/(g.K) |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric strength | K20/P50，干/湿 | 110/80 | KV/mm | |
| 23℃ | V/mil | 840 | ||
| Volume resistance | 干/湿 | 10 | Ω.cm | |
| Surface resistance | 干/湿 | 10 | Ω | |
| Dielectric constant | 1MHz，干/湿 | 3.2/5 | ||
| Volume resistivity | 23℃ | ohms·cm | 1.0E+12到1.0E+14 | |
| Relative arc track index CT1 | 干/湿 | CTI 600 | ||
| Relative Arc Track Index CTIM | 干/湿 | CTI 575 M | ||
| Loss angle | 1MHz，干/湿 | 0.025/0.2 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 11.143到19.964 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | MPa | 222.76到370.34 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.