PA66 Vydyne® 21SPC ASCEND USA

243

Unit Price:
$4329 USD/MT
Packaging Specification:
25 KG/PKG
Supply Quantity:
77MT
Delivery Terms:
FOB
Port of Loading:
China Main Port
Accepted Payment Methods:
T/T
Shipping:
Negotiate supplier for shipping details

Supplier Information

ASIA PLASTIC EXCHANGE LIMITED

+86 755 2787 3515View

serv********View

For more detailed information including pricing, customization, and shipping, please contact supplier.

Material Description

Technical Data Sheet

Material Description

Material Properties:--
Application Areas:--
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
density		ISO 1183	1.14	g/cm³
Shrinkage rate	Across Flow : 23°C, 2.00 mm	ISO 294-4	1.7	%
Shrinkage rate	Shrinkage rate	流量 : 23°C, 2.00 mm	ISO 294-4	1.8	%
Water absorption rate	24 hr, 23°C	ISO 62	1.2	%
Water absorption rate	Water absorption rate	Equilibrium, 23°C, 50% RH	ISO 62	2.4	%
Outdoor applicability	全部	UL 746C	f2

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile modulus	23°C	ISO 527-2	3100	Mpa
Tensile stress	Yield, 23°C	ISO 527-2	82.0	Mpa
Tensile stress	Tensile stress	Break, 23°C	ISO 527-2	55.0	Mpa
Tensile strain	Yield, 23°C	ISO 527-2	5.0	%
Nominal tensile fracture strain	23°C	ISO 527-2	25	%
Bending modulus	23°C	ISO 178	2900	Mpa
bending strength	23°C	ISO 178	80.0	Mpa
Poisson's ratio		ISO 527	0.40

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45 MPa, Unannealed	ISO 75-2/B	200	°C
Hot deformation temperature	Hot deformation temperature	1.8 MPa, Unannealed	ISO 75-2/A	70.0	°C
Melting temperature		ISO 11357-3	260	°C
Linear coefficient of thermal expansion	Flow : 23 to 55°C	ISO 11359-2	1.0E-4	cm/cm/°C
Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	Across Flow : 23 to 55°C	ISO 11359-2	1.0E-4	cm/cm/°C
RTI Elec	0.40 mm	UL 746	130	°C
	RTI Elec	0.71 mm	UL 746	130	°C
		RTI Elec	1.5 mm	UL 746	130	°C
		RTI Elec	RTI Elec	3.0 mm	UL 746	130	°C
RTI Imp	0.40 mm	UL 746	75.0	°C
	RTI Imp	0.71 mm	UL 746	75.0	°C
		RTI Imp	1.5 mm	UL 746	75.0	°C
		RTI Imp	RTI Imp	3.0 mm	UL 746	75.0	°C
RTI	0.40 mm	UL 746	75.0	°C
	RTI	0.71 mm	UL 746	85.0	°C
		RTI	1.5 mm	UL 746	85.0	°C
		RTI	RTI	3.0 mm	UL 746	85.0	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
Volume resistivity	0.750 mm	IEC 60093	1.0E+13	ohms·cm
Dielectric strength	1.00 mm	IEC 60243	26	KV/mm
Arc resistance	3.00 mm	ASTM D495	PLC 5
Leakage Trace Index	3.00 mm	IEC 60112	600	V
High arc combustion index (HAI)	0.40 mm	UL 746	PLC 1
	High arc combustion index (HAI)	0.71 mm	UL 746	PLC 0
		High arc combustion index (HAI)	1.5 mm	UL 746	PLC 0
		High arc combustion index (HAI)	High arc combustion index (HAI)	3.0 mm	UL 746	PLC 0
High Voltage Arc Traceability Rate (HVTR)		UL 746	PLC 0
Hot wire ignition (HWI)	0.40 mm	UL 746	PLC 4
	Hot wire ignition (HWI)	0.71 mm	UL 746	PLC 4
		Hot wire ignition (HWI)	1.5 mm	UL 746	PLC 3
		Hot wire ignition (HWI)	Hot wire ignition (HWI)	3.0 mm	UL 746	PLC 2

injection	Test Result	Unit
Mold temperature	65 到 95	°C
Processing (melt) temperature	285 到 300	°C
Spray nozzle temperature	280 到 300	°C
Temperature at the front of the material cylinder	280 到 290	°C
Temperature in the middle of the barrel	270 到 285	°C
Temperature at the rear of the barrel	260 到 280	°C
Suggested maximum recycled material ratio	50	%
drying time	1.0 到 3.0	hr
drying temperature	< 70	°C

Impact performance	Test Condition	Test Method	Test Result	Unit
Charpy Notched Impact Strength	-30°C	ISO 179/1eA	5.0	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO 179/1eA	6.0	kJ/m²
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	无断裂
Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch	23°C	ISO 179/1eU	无断裂
Impact strength of cantilever beam gap	-30°C	ISO 180	5.0	kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO 180	6.0	kJ/m²

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.40 mm	UL 94	V-2
	UL flame retardant rating	0.71 mm	UL 94	V-2
		UL flame retardant rating	1.5 mm	UL 94	V-2
		UL flame retardant rating	UL flame retardant rating	3.0 mm	UL 94	V-2
Burning wire flammability index	0.40 mm	IEC 60695-2-12	960	°C
	Burning wire flammability index	0.71 mm	IEC 60695-2-12	960	°C
		Burning wire flammability index	1.5 mm	IEC 60695-2-12	960	°C
		Burning wire flammability index	Burning wire flammability index	3.0 mm	IEC 60695-2-12	960	°C
Hot filament ignition temperature	0.40 mm	IEC 60695-2-13	825	°C
	Hot filament ignition temperature	0.71 mm	IEC 60695-2-13	850	°C
		Hot filament ignition temperature	1.5 mm	IEC 60695-2-13	850	°C
		Hot filament ignition temperature	Hot filament ignition temperature	3.0 mm	IEC 60695-2-13	850	°C
Extreme Oxygen Index		ISO 4589-2	25	%

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.