PA6 Durethan® BKV45 000000 ENVALIOR WUXI
210
Unit Price:$3550 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Filler: Glass fiber reinf 35% filler by weight
- Application Areas:--
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Apparent density | ISO60 | 0.70 | g/cm³ | |
| Shrinkage rate | TD:280°C,2.00mm2 | ISO294-4 | 0.70 | % |
| TD:120°C,2hr,2.00mm3 | ISO294-4 | 0.14 | % | |
| MD:280°C,2.00mm2 | ISO294-4 | 0.23 | % | |
| MD:120°C,2hr,2.00mm3 | ISO294-4 | 0.070 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 6.5 | % |
| Equilibrium,23°C,50%RH | ISO62 | 1.9 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2/1 | 10700 | Mpa |
| Tensile stress | Break,23°C | ISO527-2/5 | 180 | Mpa |
| Tensile strain | Break,23°C | ISO527-2/5 | 3.0 | % |
| TensileCreepModule | 1hr | ISO899-1 | -- | Mpa |
| Tensile creep modulus | 1000hr | ISO899-1 | -- | Mpa |
| Bending modulus 4 | 23°C | ISO178/A | 10700 | Mpa |
| Bending stress 4 | 3.5%Strain | ISO178/A | 280 | Mpa |
| 23°C | ISO178 | 290 | Mpa | |
| FlexuralStrainatFlexuralStrength5(23°C) | 4.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 215 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 205 | °C | |
| 8.0MPa,Unannealed | ISO75-2/C | 150 | °C | |
| Vicat softening temperature | -- | ISO306/B50 | 200 | °C |
| -- | ISO306/B120 | >200 | °C | |
| Melting temperature 5 | ISO11357-3 | 222 | °C | |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO11359-2 | 2E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 8E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+14 | ohms | |
| Volume resistivity | 23°C | IEC60093 | 1E+15 | ohms·cm |
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 40 | KV/mm |
| Relative permittivity | 23°C,100Hz | IEC60250 | 4.00 | |
| 23°C,1MHz | IEC60250 | 4.00 | ||
| Dissipation factor | 23°C,100Hz | IEC60250 | 7E-03 | |
| 23°C,1MHz | IEC60250 | 0.015 | ||
| Leakage Trace Index | SolutionA | IEC60112 | 525 | V |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Membrane puncture strength | --6 | ISO6603-2 | 3.30 | J |
| --7 | ISO6603-2 | 3.90 | J | |
| Membrane piercing force | --6 | ISO6603-2 | 945 | N |
| --7 | ISO6603-2 | 1060 | N |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 70 | kJ/m² |
| 23°C | ISO179/1eU | 80 | kJ/m² | |
| Unscented Izod impact strength | -30°C | ISO180/1U | 70 | kJ/m² |
| 23°C | ISO180/1U | 75 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | ISO2039-1 | 230 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL94 | HB | |
| 3.2mm | UL94 | HB | ||
| Burning wire flammability index | 2.0mm | IEC60695-2-12 | 650 | °C |
| Extreme Oxygen Index 9 | ISO4589-2 | 23 | % | |
| BurningBehavior10 | >1.00mm | ISO3795 | passed |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ISO Shortcut | ISO1874 | PA6,GR,14-110,GF35 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.