PA6 LNP™ LUBRICOMP™ PX11311 WH9F059 SABIC INNOVATIVE US
178
- Unit Price:
- $6073 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Dimensional stability Low Specific Gravity
- Application Areas:Automotive body panels Automotive sector
- Color:--
- Grade:Impact resistant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt volume flow rate | 300°C/10.0kg | ISO1133 | 49.0 | cm3/10min |
| Shrinkage rate | MD:24hr | ASTMD955 | 0.33 | % |
| TD:24hr | ASTMD955 | 0.48 | % | |
| 23°C,24hr | 内部方法 | 0.25 | % | |
| Balance, 23 ° C, 50% RH | ISO62 | 0.040 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus 1 | ASTMD638 | 7240 | Mpa | |
| Tensile strength 2 | Break | ASTMD638 | 52.0 | Mpa |
| Elongation rate 3 | Break | ASTMD638 | 2.0 | % |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 9050 | Mpa |
| Bending strength 5 | Break,50.0mmSpan | ASTMD790 | 76.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 199 | °C |
| Linear coefficient of thermal expansion | MD:-40to40°C | ASTME831 | 3.1E-05 | cm/cm/°C |
| MD:40to120°C | ASTME831 | 1.9E-05 | cm/cm/°C | |
| TD:-40to40°C | ASTME831 | 4.6E-05 | cm/cm/°C | |
| TD:40to120°C | ASTME831 | 7E-05 | cm/cm/°C | |
| specific heat | ASTMC351 | 1420 | J/kg/°C | |
| --6 | ASTM D790/ISO 178 | 1.2 | W/m/K | |
| --7 | ASTM D790/ISO 178 | 2.1 | W/m/K | |
| --8 | ISO22007-2 | 0.99 | W/m/K | |
| --9 | ISO22007-2 | 1.4 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ASTMD257 | >1.0E+15 | ohms | |
| Dielectric strength | 1.00mm,inOil | ASTMD149 | >10 | KV/mm |
| Dielectric constant | 1.10GHz | ASTMES7-83 | 4.74 | |
| Dissipation factor | 1.10GHz | ASTMES7-83 | 7.7E-03 | |
| Leakage Trace Index | IEC60112 | 600 | V | |
| High arc combustion index | HAI | UL746 | PLC0 | |
| Hot wire ignition | HWI | UL746 | PLC0 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO179 | 5.3到18 | kJ/m² | |
| Cantilever beam without notch impact strength | 23°C | ASTMD4812 | 180 | J/m |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.00mm | UL94 | V-0 | |
| Burning wire flammability index | 2.00mm | IEC60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 1.00mm | IEC60695-2-13 | 775 | °C |
| 3.00mm | IEC60695-2-13 | 850 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.