PA6 Durethan® BKV30 000000 LANXESS WUXI
191
- Unit Price:
- $3035 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 27MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Glass fiber reinforced Filler: Glass fiber reinf 30% Filler by weight
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD:280°C,3.00mm2 | ISO2577 | 0.82 | % |
| TD:120°C,2hr,3.00mm3 | ISO294-4 | 0.12 | % | |
| MD:280°C,3.00mm2 | ISO2577 | 0.16 | % | |
| MD:120°C,2hr,3.00mm3 | ISO2577 | 0.030 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 7.0 | % |
| Equilibrium,23°C,50%RH | ISO62 | 2.1 | % | |
| Apparent density | ISO60 | 0.70 | g/cm³ | |
| Melt volume flow rate | 260°C/5.0kg | ISO1133 | 14.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | Break,23°C | ASTMD638 | 180 | Mpa |
| Bending modulus 5 | 23°C | ISO178/A | 8600 | Mpa |
| Tensile modulus 4 | 23°C | ASTMD638 | 9200 | Mpa |
| Bending stress 5 | 3.5%Strain | ISO178/A | -- | Mpa |
| 23°C | ISO178 | 280 | Mpa | |
| FlexuralStrainatFlexuralStrength6(23°C) | 4.0 | % | ||
| Tensile stress | Break,23°C | ISO527-2/5 | 180 | Mpa |
| Tensile strain | Break,23°C | ISO527-2/5 | 3.0 | % |
| Tensile creep modulus | 1000hr | ISO899-1 | -- | Mpa |
| Tensile modulus | -5°C | ISO527-2/1 | 9800 | Mpa |
| elongation | Break,23°C | ASTMD638 | 3.0 | % |
| Bending modulus | 23°C | ASTMD790 | 8270 | Mpa |
| bending strength | 23°C | ASTMD790 | 280 | Mpa |
| TensileCreepModule | 1hr | ISO899-1 | -- | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | MD：23to55°C | ISO11359-2 | 2E-05 | cm/cm/°C |
| TD：23to55°C | ISO11359-2 | 8E-05 | cm/cm/°C | |
| RTIElec | 1.5mm | UL746 | 130 | °C |
| Evolution Calendar intelligent importer | 0.8mm | UL746 | 95.0 | °C |
| 1.5mm | UL746 | 95.0 | °C | |
| RTIStr | 0.8mm | UL746 | 130 | °C |
| 1.5mm | UL746 | 130 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed,4.00mm | ASTMD648 | 215 | °C |
| 0.45MPa,Unannealed | ISO75-2/B | 215 | °C | |
| 1.8MPa,Unannealed,4.00mm | ASTMD648 | 200 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 200 | °C | |
| Melting temperature 5 | ISO11357-3 | 222 | °C | |
| Vicat softening temperature | -- | ISO306/B50 | 200 | °C |
| -- | ISO306/B120 | >200 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dielectric constant 10 | 23°C,50Hz | IEC60250 | 4.00 | |
| 23°C,1MHz | IEC60250 | 4.00 | ||
| Surface resistivity | IEC60093 | 1E+14 | ohms | |
| Arc resistance | ASTMD495 | -- | sec | |
| Volume resistivity | 23°C | IEC60093 | 1E+15 | ohms·cm |
| Dissipation factor | 23°C,50Hz | IEC60250 | 5E-03 | |
| 23°C,100Hz | IEC60250 | 5E-03 | ||
| 23°C,1MHz | IEC60250 | 0.0150.015 | ||
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 40 | KV/mm |
| 23°C,3.00mm | IEC60243-1 | 40 | KV/mm | |
| Relative permittivity | 23°C,100Hz | IEC60250 | 4.00 | |
| 23°C,1MHz | IEC60250 | 4.00 | ||
| Leakage Trace Index | ASTMD3638 | -- | V | |
| SolutionA | IEC60112 | 600 | V | |
| SolutionB | IEC60112 | 400 | V |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Membrane puncture strength | --7 | ISO6603-2 | 8.00 | J |
| --8 | ISO6603-2 | 6.00 | J | |
| Membrane piercing force | --8 | ISO6603-2 | 950 | N |
| --7 | ISO6603-2 | 1070 | N |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unscented Izod impact strength | -30°C | ISO180/1U | 60 | kJ/m² |
| 23°C | ISO180/1U | 75 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 70 | kJ/m² |
| 23°C | ISO179/1eU | 80 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | ISO2039-1 | 210 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Extreme Oxygen Index 11 | ISO4589-2 | 22 | % | |
| BurningBehavior12 | >1.00mm | ISO3795 | passed | |
| UL flame retardant rating | 0.8mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 1.6mm | UL94 | HB | ||
| 3.0mm | UL94 | HB | ||
| 3.2mm | UL94 | HB | ||
| Burning wire flammability index | 2.0mm | IEC60695-2-12 | 600 | °C |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| ISO Shortcut | ISO1874 | PA6,GR,14-100,GF30 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.