PA6 Ultramid® B3GK24 BK00564 BASF GERMANY
209
Unit Price:$4164 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility Oil resistant Filler: glass beads fibe 30% filler by weight
- Application Areas:Thin walled components Electrical enclosure Industrial components Application in the automo Plastic accessories Shell
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | ASTMD792 | 1.34 | g/cm³ | |
| ISO1183 | 1.34 | g/cm³ | ||
| Melt volume flow rate | 275°C/5.0kg | ISO1133 | 70.0 | cm3/10min |
| Shrinkage rate | MD：3.18mm | 0.40 | % | |
| Water absorption rate | Saturation | ASTMD570 | 6.6 | % |
| Saturation,23°C | ISO62 | 6.6 | % | |
| Equilibrium,50%RH | ASTMD570 | 2.0 | % | |
| Equilibrium,23°C,50%RH | ISO62 | 2.0 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2 | 6000 | Mpa |
| Tensile strength | Break,23°C | ASTMD638 | 110 | Mpa |
| Tensile stress | Break,23°C | ISO527-2 | 105 | Mpa |
| Tensile strain | Break,23°C | ISO527-2 | 3.5 | % |
| Bending modulus | 23°C | ASTMD790 | 4830 | Mpa |
| Kabi impact strength | +23℃,干/湿 | 40/90 | KJ/m | |
| Fracture stress (V=50mm/min) | 干/湿 | 110/65 | Mpa | |
| Tensile yield stress (V=50mm/min) | 干/湿 | 110/65 | Mpa | |
| Elongation at break (V=50mm/min) | 干/湿 | 3.5/15 | % | |
| Kabi impact strength | 30℃干 | 39 | KJ/m | |
| Tensile modulus of elasticity | 干/湿 | 6000/3000 | Mpa | |
| Ball pressure hardness | 干/湿 | 170/120 | Mpa | |
| Kapi notch impact strength | 30℃，干/湿 | 5 | KJ/m | |
| Izo notch impact strength | +23℃，干/湿 | 5/8.5 | KJ/m | |
| Yield elongation (V=50mm/min) | 干/湿 | 3.5/15 | % | |
| Tensile creep modulus | 1000h,湿 | 2000 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Thermal conductivity | Dry | 0.34 | W/(m.K) | |
| Linear coefficient of thermal expansion | （23-80）℃，Dry | 3.5-4 | ||
| Hot deformation temperature | 0.45MPa负荷，Dry | 215 | °C | |
| Maximum operating temperature | 200 | °C | ||
| Specific heat capacity | Dry | 1.4 | J/(g.K) | |
| Hot deformation temperature | 1.8MPa负荷，Dry | 200 | °C | |
| 0.45MPa,Unannealed | ASTMD648 | 215 | °C | |
| 0.45MPa,Unannealed | ISO75-2/B | 215 | °C | |
| 1.8MPa,Unannealed | ASTMD648 | 200 | °C | |
| 1.8MPa,Unannealed | ISO75-2/A | 200 | °C | |
| Peak melting temperature | ASTMD3418 | 220 | °C | |
| Melting temperature (DSC) | ISO3146 | 220 | °C | |
| Linear coefficient of thermal expansion | MD | ASTME831 | 1E-05 | cm/cm/°C |
| MD | 3.8E-05 | cm/cm/°C | ||
| RTIElec | 0.75mm | UL746 | 65.0 | °C |
| 1.5mm | UL746 | 65.0 | °C | |
| 3.0mm | UL746 | 65.0 | °C | |
| Evolution Calendar intelligent importer | 0.75mm | UL746 | 65.0 | °C |
| 1.5mm | UL746 | 65.0 | °C | |
| 3.0mm | UL746 | 65.0 | °C | |
| RTIStr | 0.75mm | UL746 | 65.0 | °C |
| 1.5mm | UL746 | 65.0 | °C | |
| 3.0mm | UL746 | 65.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| VolumeResistivity | 1.50mm | ASTMD257 | 1E+15 | ohms·cm |
| Volume resistivity | IEC60093 | 1E+15 | ohms·cm | |
| Dielectric constant | 1MHz | IEC60250 | 3.90 | |
| Dissipation factor | 1MHz | IEC60250 | 0.020 | |
| Leakage Trace Index | IEC60112 | 425 | V | |
| Relative arc track index CT1 | 干/湿 | CTI 425 | ||
| bending strength | 干/湿 | 175/100 | Mpa | |
| Volume resistance | 干/湿 | 10 | Ω.cm | |
| Surface resistance | 干/湿 | 10 | Ω | |
| Dielectric strength | K20/P50，干/湿 | 135/53 | KV/mm | |
| Loss angle | 1MHz，干/湿 | 0.02/0.07 | ||
| Dielectric constant | 1MHz，干/湿 | 3.9/4.6 | J/(g.K) |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | 37 | J/m |
| Charpy Notched Impact Strength | -30°C | ISO179 | 5.0 | kJ/m² |
| 23°C | ISO179 | 5.0 | kJ/m² | |
| Impact strength of simply supported beam without notch | -30°C | ISO179 | 39 | kJ/m² |
| 23°C | ISO179 | 40 | kJ/m² | |
| Impact strength of cantilever beam gap | -40°C | ASTMD256 | 32 | J/m |
| Other performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact and destructive energy | 干/湿 | 5/25 | J |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 3.0mm | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.