| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|
| density | | ASTM D792/ISO 1183 | 1.36 | |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Apparent density | | ISO60 | 0.60 | g/cm³ |
| Shrinkage rate | TD:280°C,2.00mm2 | ISO294-4 | 0.81 | % |
| Shrinkage rate | TD:120°C,2hr,2.00mm3 | ISO294-4 | 0.10 | % |
| Shrinkage rate | MD:280°C,2.00mm2 | ISO294-4 | 0.29 | % |
| Shrinkage rate | MD:120°C,2hr,2.00mm3 | ISO294-4 | 0.050 | % |
| Water absorption rate | Saturation,23°C | ISO62 | 7.0 | % |
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 2.1 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile stress | Break,23°C | ISO527-2/5 | 170 | Mpa |
| Tensile strain | Break,23°C | ISO527-2/5 | 3.0 | % |
| Tensile modulus | | ASTM D638/ISO 527 | 9910 | kg/cm²(MPa)[Lb/in²] |
| Tensile modulus | 23°C | ASTMD638 | 8730 | Mpa |
| Tensile modulus | 23°C | ISO527-2/1 | 9400 | Mpa |
| tensile strength | | ASTM D638/ISO 527 | 175 | kg/cm²(MPa)[Lb/in²] |
| elongation | Break,23°C | ASTMD638 | 3.2 | % |
| Bending modulus | 23°C | ASTMD790 | 8000 | Mpa |
| Bending modulus | | ASTM D790/ISO 178 | 9120 | kg/cm²(MPa)[Lb/in²] |
| bending strength | | ASTM D790/ISO 178 | 276 | kg/cm²(MPa)[Lb/in²] |
| bending strength | 23°C | ASTMD790 | 260 | Mpa |
| Tensile strength | Break,23°C | ASTMD638 | 165 | Mpa |
| Bending stress 4 | 3.5%Strain | ISO178/A | 255 | Mpa |
| Bending stress 4 | 23°C | ISO178 | 260 | Mpa |
| Bending stress 4 | FlexuralStrainatFlexuralStrength5(23°C) | | 3.6 | % |
| Bending modulus 4 | 23°C | ISO178/A | 8400 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Vicat softening temperature | | ISO306/B120 | 210 | °C |
| BallPressure Test | 210°C | IEC60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：23to55°C | ISO11359-2 | 2E-05 | cm/cm/°C |
| Linear coefficient of thermal expansion | TD：23to55°C | ISO11359-2 | 1E-04 | cm/cm/°C |
| Combustibility (rate) | | UL94 | HB | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 219 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 210 | °C |
| Hot deformation temperature | 8.0MPa,Unannealed | ISO75-2/C | 150 | °C |
| vicat softening point | | ASTM D1525/ISO R306 | 210 | ℃（℉） |
| Melting temperature 5 | | ISO11357-3 | 221 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Leakage Trace Index | SolutionA | IEC60112 | 400 | V |
| Dielectric strength | 23°C,1.00mm | IEC60243-1 | 33 | KV/mm |
| film | Test Condition | Test Method | Test Result | Unit |
|---|
| Membrane puncture strength | --6 | ISO6603-2 | 2.10 | J |
| Membrane puncture strength | --7 | ISO6603-2 | 2.20 | J |
| Membrane piercing force | --6 | ISO6603-2 | 744 | N |
| Membrane piercing force | --7 | ISO6603-2 | 803 | N |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Unscented Izod impact strength | 23°C | ISO180/1U | 60 | kJ/m² |
| Unscented Izod impact strength | -30°C | ISO180/1U | 55 | kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 55 | kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 65 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|
| Ball pressure hardness | | ISO2039-1 | 193 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| BurningBehavior9 | | ISO3795 | passed | |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|
| ISO Shortcut | | ISO1874 | PA6,GHR,10-090,GF30 | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.