PA6 Ultramid® B3WG10 BASF GERMANY
198
- Unit Price:
- $4231 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Thermal stability High mobility High rigidity Heat aging
- Application Areas:Industrial components
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.55 | ||
| Molding shrinkage rate | ASTM D955 | 0.3 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Fracture stress (V=50mm/min) | 干/湿 | 235/160 | Mpa | |
| Kapi notch impact strength | 30℃，干/湿 | 16 | KJ/m | |
| Impact and destructive energy | +23℃，干/湿 | 3/10 | J | |
| Bending modulus | 干/湿 | 15000/9000 | Mpa | |
| Kabi impact strength | 30℃，干 | 90 | KJ/m | |
| Kapi notch impact strength | 干/湿 | 22/30 | KJ/m | |
| Kabi impact strength | +23℃，干/湿 | 100/110 | KJ/m | |
| Yield elongation (V=50mm/min) | 干/湿 | 3/5.5 | % | |
| Tensile yield stress (V=50mm/min) | 干/湿 | 235/160 | Mpa | |
| Ball pressure hardness | 干/湿 | 280/210 | Mpa | |
| Izo notch impact strength | +23℃，干/湿 | 20/24 | KJ/m | |
| elongation | ≤0.5%, +23℃，湿 | 7400 | Mpa | |
| bending strength | 干/湿 | 320/240 | Mpa | |
| Tensile creep modulus | 1000h，湿 | 7400 | Mpa | |
| Elongation at break (V=50mm/min) | 干/湿 | 3/5.5 | % | |
| Tensile modulus of elasticity | 干/湿 | 16000/11000 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | （23-80）℃，Dry | 1-1.5/5-6 | ||
| Hot deformation temperature | 1.8MPa负荷，Dry | 215 | °C | |
| Maximum operating temperature | 200 | °C | ||
| Temperature index | 在20000h/5000h，后拉伸强度下降50%时 | 130/160 | °C | |
| Thermal conductivity | Dry | 0.32 | W/(m.K) | |
| Hot deformation temperature | 0.45MPa负荷,Dry | 220 | °C | |
| Specific heat capacity | Dry | 1.3 | J/(g.K) |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistance | 干/湿 | 10 | Ω | |
| Relative arc track index CT1 | 干/湿 | CTI 450 | ||
| Volume resistance | 干/湿 | 10 | Ω.cm | |
| Dielectric strength | K20/P50，干/湿 | 90/40 | KV/mm | |
| Dielectric constant | 1MHz，干/湿 | 4.2/6.1 | ||
| Loss angle | 1MHz，干/湿 | 0.014/0.14 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.