PA6 Ultramid® B3EG6 BASF GERMANY
280
- Unit Price:
- $2257 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 224MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Oil resistant Filler: Glass fiber reinf 30% filler by weight
- Application Areas:Electronic insulation Industrial applications Electronic insulation Industrial applications
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | ISO1183 | 1.36 | g/cm³ | |
| Water absorption rate | (23°C,24hr) | ISO62 | 6.00 | % |
| (23°C,50RH) | ISO62 | 2.10 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | 23°C | ISO527-2 | 180 | Mpa |
| elongation at break | 23°C | ISO527-2 | 3.0 | % |
| Tensile modulus | 23°C | ISO527-2 | 9500 | Mpa |
| Bending modulus | 23°C | ISO178 | 8600 | Mpa |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 10 | kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 10 | kJ/m² |
| -30°C | ISO180/1A | 8.4 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPaUnannealed | ISO75-2/Bf | 220 | °C |
| 1.80MPaAnnealed | ISO75-2/Af | 210 | °C | |
| Vicat softening temperature | Melting Temperature | ISO11357-3 | 220 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistance | IEC60093 | 1E+13 | Ω.cm | |
| Dielectric constant | 23°C | IEC60250 | 3.80 | 1MHz |
| Dissipation factor | 23°C | IEC60250 | 0.025 | 100HZ |
| 23°C | IEC60250 | 0.025 | 1MHz | |
| 相对漏电起痕指数 | IEC60112 | 550 | V |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | ISO2039-1 | 181 | Mpa |
| Flame retardant performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Fire rating | UL-94 | 1.50mm | HB | |
| UL-94 | 2.00mm | HB | ||
| UL-94 | 3.00mm | HB | ||
| Ignition temperature of heating wire | 1.00mm | IEC60695-2-12 | 750 | °C |
| 2.00mm | IEC60695-2-12 | 800 | °C | |
| 3.00mm | IEC60695-2-12 | 750 | °C | |
| Relative temperature of heating wire | 1.00mm | IEC60695-2-13 | 725 | °C |
| 2.00mm | IEC60695-2-13 | 775 | °C | |
| 3.00mm | IEC60695-2-13 | 725 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.