PA6 Amilan® CM1017 TORAY JAPAN
252
- Unit Price:
- $3684 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 51.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High hardness
- Application Areas:Electrical components Electrical appliances Automotive sector Shell
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.13 | ||
| Water absorption rate 23 ℃/24h | ASTM D570/ISO 62 | 1.8 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：1.00mm3 | % | 0.50到1.0 | -- |
| MD：3.00mm4 | % | 1.0到1.6 | -- | |
| Water absorption rate | 23°C,24hr | % | 1.8 | -- |
| Saturation,23°C | % | 11 | -- | |
| Taber wear amount | 1000g,CS-17 | ASTM D-1044 | 无水｜3-4 | mg/1000次 |
| 1000g,CS-17 | ASTM D-1044 | 3.5%水｜- | mg/1000次 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | -40°C | MPa | 120 | 115 |
| 23°C | MPa | 85.0 | 40.0 | |
| Tensile fracture strength | 23℃ | ASTM D-638 | 无水｜20 | kg/cm2 |
| 23℃ | ASTM D-638 | 3.5%水｜- | kg/cm2 | |
| Rockwell hardness | ASTM D785 | 83 | ||
| Tensile yield strength | 23℃ | ASTM D-638 | 无水｜820 | kg/cm2 |
| 23℃ | ASTM D-638 | 3.5%水｜420 | kg/cm2 | |
| 80℃ | ASTM D-638 | 无水｜320 | kg/cm2 | |
| 80℃ | ASTM D-638 | 3.5%水｜220 | kg/cm2 | |
| -40 | ASTM D-638 | 无水｜1230 | kg/cm2 | |
| -40 | ASTM D-638 | 3.5%水｜1150 | kg/cm2 | |
| Flexural modulus | -40℃ | ASTM D-790 | 无水｜40000 | kg/cm2 |
| -40℃ | ASTM D-790 | 3.5%水｜37000 | kg/cm2 | |
| Tensile stress | 80°C | MPa | 30.0 | 20.0 |
| Tensile strain | Yield,23°C | % | 1.5 | -- |
| Break,23°C | % | 38 | ||
| Bending modulus | -40°C | MPa | 3900 | 3600 |
| 23°C | MPa | 3000 | 1000 | |
| 80°C | MPa | 800 | 400 | |
| Bending stress | -40°C | MPa | 145 | 140 |
| 23°C | MPa | 120 | 45.0 | |
| 80°C | MPa | 50.0 | 30.0 | |
| Compressive stress | 23°C | MPa | 85.0 | -- |
| shear strength | 23°C | MPa | 75.0 | 70.0 |
| Taber abraser | 1000Cycles | mg | 3.00到4.00 | -- |
| Friction coefficient vs. Metal5 | 0.15到0.20 | -- | ||
| Flexural modulus | 23℃ | ASTM D-790 | 无水｜29000 | kg/cm2 |
| 23℃ | ASTM D-790 | 3.5%水｜10000 | kg/cm2 | |
| compressive strength | 23℃ | ASTM D-695 | 无水｜890 | kg/cm2 |
| 23℃ | ASTM D-695 | 3.5%水｜- | kg/cm2 | |
| Rockwell hardness | 23℃ | ASTM D-785 | 无水｜83 | M-标度 |
| 23℃ | ASTM D-785 | 3.5%水｜- | M-标度 | |
| Flexural strength | 23℃ | ASTM D-790 | 无水｜1100 | kg/cm2 |
| 23℃ | ASTM D-790 | 3.5%水｜450 | kg/cm2 | |
| Flexural modulus | 80℃ | ASTM D-790 | 无水｜8000 | kg/cm2 |
| 80℃ | ASTM D-790 | 3.5%水｜4000 | kg/cm2 | |
| elongation at break | 23℃ | ASTM D-638 | 无水｜180 | % |
| 23℃ | ASTM D-638 | 3.5%水｜<200 | % | |
| Shear strength | 23℃ | ASTM D-732 | 无水｜740 | kg/cm2 |
| 23℃ | ASTM D-732 | 3.5%水｜690 | kg/cm2 | |
| Flexural strength | 80℃ | ASTM D-790 | 无水｜500 | kg/cm2 |
| 80℃ | ASTM D-790 | 3.5%水｜300 | kg/cm2 | |
| -40℃ | ASTM D-790 | 无水｜1500 | kg/cm2 | |
| -40℃ | ASTM D-790 | 3.5%水｜1450 | kg/cm2 | |
| Rockwell hardness | 23℃ | ASTM D-785 | 无水｜119 | R-标度 |
| 23℃ | ASTM D-785 | 3.5%水｜90 | R-标度 | |
| IZOD impact strength | 23℃，Unnotched1/8 | 无水｜无断裂 | kg.cm/cm | |
| 23℃，Unnotched1/8 | 3.5%水｜- | kg.cm/cm | ||
| Unnotched1/2"，23℃ | 无水｜5 | kg.cm/cm | ||
| Unnotched1/2"，23℃ | 3.5%水｜40 | kg.cm/cm | ||
| -40℃，Unnotched1/2 | 无水｜3.5 | kg.cm/cm | ||
| -40℃，Unnotched1/2 | 3.5%水｜15 | kg.cm/cm |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| melting point | 差示扫描测热计DSC法 | 3.5%水｜- | °C | |
| UL-94 flame retardant grade | UL 94 | 无水｜V-2(1/16") | ||
| UL 94 | 3.5%水｜- | |||
| heat deflection temperature | 18.6kg/cm2 | ASTM D-648 | 无水｜190 | °C |
| 18.6kg/cm2 | ASTM D-648 | 3.5%水｜- | °C | |
| thermal conductivity | 无水｜0.18 | Kcal/m.hr.°C | ||
| 3.5%水｜- | Kcal/m.hr.°C | |||
| Linear coefficient of thermal expansion | ASTM D-696 | 无水｜8 | 10-5cm/cm.℃ | |
| ASTM D-696 | 3.5%水｜- | |||
| specific heat | 无水｜0.46 | Cal/g.°C | ||
| 3.5%水｜- | Cal/g.°C | |||
| heat deflection temperature | ASTM D-648 | 无水｜190 | °C | |
| ASTM D-648 | 3.5%水｜- | °C | ||
| melting point | 差示扫描测热计DSC法 | 无水｜225 | °C | |
| Hot deformation temperature | ASTM D648/ISO 75 | 190 | ℃（℉） | |
| melting point | 225 | ℃（℉） | ||
| Hot deformation temperature | 0.45MPa,Unannealed | °C | 190 | -- |
| Melting temperature | °C | 225 | -- | |
| Linear coefficient of thermal expansion | MD | cm/cm/°C | 8E-05 | -- |
| specific heat | J/kg/°C | 1900 | -- | |
| thermal conductivity | W/m/K | 0.25 | -- |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | ohms·cm | 1.0E+14到1.0E+15 | 1.0E+11到1.0E+12 | |
| Dielectric strength | kV/mm | 20 | -- | |
| Dielectric constant 6 | 23°C,50Hz | 4.10 | 9.00 | |
| 23°C,1kHz | 3.90 | 8.00 | ||
| 23°C,1MHz | 3.40 | 4.50 | ||
| Dissipation factor 6 | 23°C,50Hz | 0.070 | 0.10 | |
| 23°C,1kHz | 0.060 | 0.11 | ||
| 23°C,1MHz | 0.030 | 0.13 | ||
| Volume resistivity | ASTM D257/IEC 60093 | 10^12~13 | Ω.cm | |
| Arc resistance 7 | sec | 120 | -- | |
| Compared to the anti leakage trace index | CTI | V | 600 | -- |
| Dielectric constant | 106Hz | ASTM D-150 | 无水｜3.4 | |
| Volume resistivity | ASTM D-257 | 无水｜1014-1015 | Ω.cm | |
| ASTM D-257 | 3.5%水｜1011-1012 | Ω.cm | ||
| Loss factor | 106Hz | ASTM D-150 | 无水｜0.03 | |
| 106Hz | ASTM D-150 | 3.5%水｜- | ||
| Dielectric strength | 1/8" | ASTM D-149 | 无水｜20 | KV/mm |
| 1/8" | ASTM D-149 | 3.5%水｜- | KV/mm | |
| Loss factor | 50Hz | ASTM D-150 | 无水｜0.07 | |
| 50Hz | ASTM D-150 | 3.5%水｜- | ||
| IEC conductivity trace index | UL 746 | 无水｜≤600 | V | |
| UL 746 | 3.5%水｜- | V | ||
| Dielectric constant | 106Hz | ASTM D-150 | 无水｜3.9 | |
| 106Hz | ASTM D-150 | 3.5%水｜- | ||
| Loss factor | 103Hz | ASTM D-150 | 无水｜0.06 | |
| 103Hz | ASTM D-150 | 3.5%水｜- | ||
| Arc resistance | 1/8" | ASTM D-150 | 无水｜121 | |
| 1/8" | ASTM D-150 | 3.5%水｜- | ||
| Dielectric constant | 50HZ | ASTM D-150 | 无水｜4.1 | |
| 50HZ | ASTM D-150 | 3.5%水｜- |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -40°C | 无断裂 | -- | |
| 23°C | 无断裂 | -- |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Sale,23°C | 119 | ||
| R-Sale,80°C | 83 | -- |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.79mm | V-2 | -- |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Water absorption rate | 23℃，24hr | ASTM D-570 | 无水｜1.8 | % |
| 23℃，24hr | ASTM D-570 | 3.5%水｜- | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.