PP 6936G2 EXXONMOBIL USA
209
Unit Price:$1953 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 50MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility
- Application Areas:Personal care Industrial applications Filter material Filter material Melt blown non-woven fabr Medical/nursing supplies
- Color:--
- Grade:Extrusion grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Flow: 23 ℃ | mm/mm | 139.7E-3到0.432 | ||
| 230°C/2.16kg | g/10min | 0.95到20 | ||
| Lateral flow: 23 ℃ | mm/mm | 0.279到0.457 | ||
| 230°C/2.16kg | g/10min | 4.9到21 | ||
| 23℃,24hr | % | 0.030到0.050 | ||
| Melt volume flow rate | 230°C/2.16kg | ISO 527-2/5, ISO 527-2/50 | 0.01到0.07 | |
| 23℃ | g/cm³ | 0.969到1.25 | ||
| % | 0.87到1.2 | |||
| 23℃,24hr | % | 0.020到0.052 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Yield, 23 ℃ | MPa | 27.93到35.24 | ||
| Fracture, 23 ℃ | MPa | 21.72到30.28 | ||
| Yield, 23 ℃ | % | 1.7到8.4 | ||
| Fracture, 23 ℃ | % | 3.7到31 | ||
| 23℃ | MPa | 1841.38到4220.69 | ||
| Yield, 23 ℃ | % | 2.6到7.2 | ||
| 23℃ | MPa | 1979.31到4220.69 | ||
| MPa | 44.76到50.62 | |||
| Fracture, 23 ℃ | MPa | 44.76到59.03 | ||
| 23℃ | MPa | 33.79到62.48 | ||
| Fracture, 23 ℃ | % | 2.0到31 | ||
| Yield, 23 ℃ | MPa | 28.41到36.76 | ||
| Fracture, 23 ℃ | MPa | 19.03到32.83 | ||
| 23℃ | MPa | 1875.86到4324.14 | ||
| MPa | 30.0到35.52 | |||
| MPa | 1400.0到4703.45 | |||
| Yield, 23 ℃ | MPa | 51.38到55.59 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| -- | °C | 160 | ||
| 0.45MPa, unannealed | °C | 109到133 | ||
| 1.8MPa, unannealed | °C | 58到91 | ||
| 0.45MPa, unannealed | °C | 110到139 | ||
| -- | °C | 165到182 | ||
| mm/mm/°C | 83.8E-5到101.6E-5 | |||
| °C | 88到157 | |||
| °C | 85到156 | |||
| 1.8MPa, unannealed | °C | 59到91 |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | ohms | 1.0E+14到1.0E+15 | ||
| Leakage Trace Index | V | 596到600 | ||
| 23℃ | ohms·cm | 9.8E+15到1.0E+16 | ||
| ohms·cm | 1.0E+13到1.0E+15 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23℃ | kJ/m² | 2.229到8.821 | |
| 23℃ | kJ/m² | 1.858到2.089 | ||
| Falling hammer impact | 23℃ | N.m | 8.85到80.35 | |
| 23℃ | J/m | 0.070到0.203 | ||
| kJ/m² | 0.442到1.347 | |||
| J/m | 0.007到0.013 | |||
| Falling hammer impact | 23℃ | N.m | 26.55到73.89 |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | 23℃ | 84到106 | ||
| Ball pressure hardness | MPa | 74.48到85.52 | ||
| 23℃ | 63到78 | |||
| 72到79 |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Gardner glossiness | 46到47 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot filament ignition temperature | °C | 548到804 | ||
| Burning wire flammability index | °C | 643到960 | ||
| Extreme Oxygen Index | % | 21 | ||
| Burning rate | mm/min | 0.0到101.6 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.