PP ExxonMobil™ AP03B EXXONMOBIL USA
225
- Unit Price:
- $1230 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 80MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High impact resistance High mobility Easy to process High crystallinity High rigidity Fast forming cycle Impact resistance Block copolymerization
- Application Areas:Industrial applications Home appliance components Automotive sector Automotive interior parts Consumer goods sector
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| tensile strength | 2 in/min,50mm/min | ASTM D-638 | 26 | Mpa |
| elongation at yield | 2in/min,50mm/min | 5 | % | |
| impact strength | -29℃(-20℉) | 19 | J/m | |
| Bending modulus | 1% secant,1.3mm/min | ASTM D-790A | 1270 | Mpa |
| Izod impact strength | @23℃ | ASTM D-256A | 78 | J/m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | @66psi，455Kpa | ASTM D-648 | 115 | °C |
| Typical processing temperature | 200-230 | °C |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | ASTM D-792 | 0.90 | g/cm³ | |
| Melt index | 230℃/2.16kg | ASTM D-1238 | 30 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.