AS(SAN) Pocan® 552485 LANXESS GERMANY
269
- Unit Price:
- $1778 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Mold shrinkage rate | ASTM D-955 | 0.3-0.4 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | Speed 1mm/min | ISO 527 | 3.7 | GPa |
| Tensile yield strength | Speed 50mm/min | ISO 527 | 68 | Mpa |
| Rockwell hardness | t=6.4mm | ISO 2039-2 | 126 | R scale |
| bending strength | Speed 2mm/min | ISO 178 | 111 | Mpa |
| IZOD notch impact strength | 23℃ | ISO 180 | 2.0 | KJ/m |
| Tensile fracture strength | Speed 50mm/min | ISO 527 | 3.2 | % |
| Bending modulus | Speed 2mm/min | ISO 178 | 2.8 | GPa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | Method B | ISO 75 | 96 | °C |
| Flame retardancy | UL 94 | HB | ||
| Hot deformation temperature | Method A | ISO 75 | 84 | °C |
| Vicat softening temperature | 5kg,120℃/hr | ISO 306 | 104 | °C |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Density/specific gravity | Natural | ISO 1183 | 1.08 | g/cm |
| Melt index | 220℃,10kg | ISO 1133 | 23 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.