ABS Novodur® HH-106 BK10009 INEOS STYRO THAILAND
164
- Unit Price:
- $2807 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 43MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:heat-resisting
- Application Areas:Electronic field Automotive sector Application in the automo Automotive interior parts
- Color:--
- Grade:Heat resistant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD | ASTMD955 | 0.55 | % |
| ISO294-4 | 0.40to0.70 | % | ||
| Water absorption rate | Equilibrium,23°C,50%RH | ISO62 | 0.25 | % |
| ASTM D570 | 0.3 | % | ||
| Melt mass flow rate | 220°C/10.0kg | ASTMD1238 | 7.0 | g/10min |
| Melt volume flow rate | 220°C/10.0kg | ISO1133 | 7.00 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Yield elongation rate | ISO 527-2 | 3.0 | % | |
| Ball pressure hardness | ISO2039-1 | 102 | Mpa | |
| Vicat softening temperature | ISO 306 | 103 | °C | |
| Tensile strength at break | ISO 527-2 | 390 | kg/cm | |
| Yield tensile strength | ISO 527-2 | 520 | kg/cm | |
| Nominal tensile fracture strain | 23°C | ISO527-2 | 9.0 | % |
| Tensile strength | Yield,23°C | ASTMD638 | 52.0 | Mpa |
| Bending stress | ISO178 | 72.0 | Mpa | |
| Tensile stress | Yield,23°C | ISO527-2 | 51.0 | Mpa |
| Tensile strain | Yield,23°C | ISO527-2 | 3.0 | % |
| Tensile modulus | ISO 527-2 | 25000 | kg/cm | |
| ASTMD638 | 2500 | Mpa | ||
| ISO527-2 | 2400 | Mpa | ||
| elongation | Break | ISO 527-2 | 25 | % |
| Break | ASTMD638 | 3.0 | % | |
| Rockwell hardness | 110 | R | ||
| Bending modulus | ISO 178 | 24000 | kg/cm | |
| ASTMD790 | 2400 | Mpa | ||
| ISO178 | 2400 | Mpa | ||
| bending strength | ASTMD790 | 77.2 | Mpa | |
| ISO 178 | 770 | kg/cm |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 9E-05 | cm/cm/°C |
| Vicat softening temperature | -- | ISO306/A50 | 115 | °C |
| -- | ISO306/B50 | 106 | °C | |
| Hot deformation temperature 2 | 0.45MPa,Annealed | ISO75-2/B | 107 | °C |
| 1.8MPa,Annealed | ISO75-2/A | 99.0 | °C | |
| Maximum operating temperature | 85 | °C | ||
| thermal conductivity | DIN52612 | 0.17 | W/m/K |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Electrical strength | 1.50mm | IEC60243-1 | 39 | KV/mm |
| Leakage Trace Index | IEC60112 | 600 | V | |
| Volume resistivity | ASTMD257 | >1.0E+15 | ohms·cm | |
| IEC60093 | 1E+15 | ohms·cm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179 | 100 | kJ/m² |
| 23°C | ISO179 | 190 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.