ABS CYCOLAC™ MG37EPN-NA1000 SABIC INNOVATIVE US
131
- Unit Price:
- $2333 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:High mobility High temperature resistan
- Application Areas:Electrical applications Automotive Applications small home appliances
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM-D792 | 1.05 | g/cm | |
| Mold shrinkage rate | ASTM-D955 | 0.4-0.6 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ASTM-D638 | 2380 | Mpa | |
| tensile strength | ASTM-D638 | 33.8 | Mpa | |
| elongation | 断裂 | ASTM-D638 | 30 | % |
| Bending modulus | ASTM-D790 | 2450 | Mpa | |
| bending strength | ASTM-D790 | 73.1 | Mpa | |
| IZOD notch impact strength | 23℃ | ASTM-D256 | 347 | J/m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.80Mpa Unannealed,3.20mm | ASTM-D648 | 85 | ℃ |
| Vicat softening temperature | ASTM-D1525 | 101 | ℃ |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index | 230℃/3.8kg | ASTM-D1238 | 4.4 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.