ABS XR-404 LG CHEM KOREA
250
- Unit Price:
- $2469 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 80MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:heat-resisting
- Application Areas:Electrical/Electronic App Electrical field Electronic field Automotive sector Automotive interior parts Automotive External Parts Shell
- Color:--
- Grade:Heat resistant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt volume flow rate | 220°C/10.0kg | ISO1133 | 7.00 | cm3/10min |
| Shrinkage rate | MD：3.20mm | ASTMD955 | 0.40to0.70 | % |
| MD：3.20mm | ISO294-4 | 0.40to0.70 | % | |
| Density/specific gravity | ASTMD792 | 1.05 | g/cm³ | |
| ISO1183 | 1.05 | g/cm³ | ||
| Melt mass flow rate | 220°C/10.0kg | ASTMD1238 | 7.0 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2/1 | 2450 | Mpa | |
| Tensile strength 2 | Yield,3.20mm | ASTMD638 | 52.0 | Mpa |
| Tensile stress | Yield | ISO527-2/50 | 54.0 | Mpa |
| Elongation rate 2 | Break,3.20mm | ASTMD638 | 20 | % |
| Bending modulus 3 | 3.20mm | ASTMD790 | 2650 | Mpa |
| Bending modulus 4 | ISO178 | 2550 | Mpa | |
| FlexuralStrength3 | 3.20mm | ASTMD790 | 84.3 | Mpa |
| Bending stress 4 | ISO178 | 82.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPa,Unannealed,6.40mm | ASTMD648 | 111 | °C |
| Hot deformation temperature 5 | 0.45MPa,Unannealed,4.00mm | ISO75-2/Be | 101 | °C |
| Hot deformation temperature | 1.8MPa,Unannealed,6.40mm | ASTMD648 | 102 | °C |
| Hot deformation temperature 5 | 1.8MPa,Unannealed,4.00mm | ISO75-2/Ae | 93.0 | °C |
| Vicat softening temperature | ASTMD15256 | 112 | °C | |
| ISO306/B50 | 112 | °C | ||
| Linear coefficient of thermal expansion | MD：23to60°C | ISO11359-2 | 8.0E-5to9.0E-5 | cm/cm/°C |
| TD：23to60°C | ISO11359-2 | 8.0E-5to9.0E-5 | cm/cm/°C | |
| RTIElec | UL746 | 60.0 | °C | |
| Evolution Calendar intelligent importer | UL746 | 60.0 | °C | |
| RTIStr | UL746 | 60.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Volume resistivity | 23°C | ASTMD257 | 1.5E+03 | ohms·cm |
| Dielectric strength | 23°C,1.00mm | ASTMD149 | 33 | KV/mm |
| Arc resistance | ASTMD495 | PLC6 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 6.0 | kJ/m² |
| 23°C | ISO179/1eA | 12 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C,3.20mm | ASTMD256 | 59 | J/m |
| -30°C,6.40mm | ASTMD256 | 49 | J/m | |
| 23°C,3.20mm | ASTMD256 | 160 | J/m | |
| 23°C,6.40mm | ASTMD256 | 140 | J/m | |
| -30°C | ISO180/1A | 6.0 | kJ/m² | |
| 23°C | ISO180/1A | 13 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | ISO2039-2 | 114 | ||
| R-Scale | ASTMD785 | 112 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL94 | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.