ABS UMG ABS® TM-25M UMG JAPAN
216
Unit Price:$4839 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:heat-resisting
- Application Areas:--
- Color:--
- Grade:Heat resistant grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index (flow coefficient) | ASTM D1238/ISO 1133 | 4 | g/10min | |
| density | ASTM D792/ISO 1183 | 1.06 | ||
| Molding shrinkage rate | ASTM D955 | 0.4~0.6 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt volume flow rate | 220°C/10.0kg | ISO1133 | 4.00 | cm3/10min |
| Shrinkage rate | MD：23°C | ISO294-4 | 0.40到0.60 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2 | 2400 | Mpa |
| Tensile stress | 23°C | ISO527-2 | 45.0 | Mpa |
| Bending modulus 3 | 23°C | ISO178 | 2500 | Mpa |
| Bending stress 3 | 23°C | ISO178 | 66.0 | Mpa |
| Charpy impact strength | 17 | KJ/m | ||
| Bending modulus | 2500 | Mpa | ||
| Tensile modulus | ASTM D638/ISO 527 | 2400 | kg/cm²(MPa)[Lb/in²] | |
| tensile strength | ASTM D638/ISO 527 | 45 | kg/cm²(MPa)[Lb/in²] | |
| Rockwell hardness | ASTM D785 | 113 | ||
| Bending modulus | ASTM D790/ISO 178 | 2500 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 66 | kg/cm²(MPa)[Lb/in²] | |
| IZOD notch impact strength | ASTM D256/ISO 179 | 11 | kg·cm/cm(J/M)ft·lb/in | |
| ASTM D256/ISO 179 | 17 | kg·cm/cm(J/M)ft·lb/in |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 98 | °C | ||
| Flame retardant grade | UL94 | HB | ||
| Combustibility (rate) | UL94 | 1.5 HB | ||
| Hot deformation temperature | ASTM D648/ISO 75 | 98 | ℃（℉） | |
| Linear expansion coefficient | ASTM D696/ISO 11359 | 9 | mm/mm.℃ | |
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/Af | 98.0 | °C |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 9E-05 | cm/cm/°C |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Sale,23°C | ISO2039-2 | 113 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL94 | HB |
| Basic performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt index | 4 | g/10min |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.