PBT VALOX™ VX5011-7001 SABIC INNOVATIVE SHANGHAI
23
- Unit Price:
- $2840 USD/MT
- Packaging Specification:
- Supply Quantity:
- 15MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low warpage Aging resistance Filler: Glass fiber reinf 10% filler by weight 10% filler by weight
- Application Areas:packing Electronic and Electrical
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 265°C/5.0kg | ASTMD1238 | 85 | g/10min |
| 266°C/5.0kg | ASTMD1238 | 85 | g/10min | |
| Melt volume flow rate | 250°C/2.16kg | ISO1133 | 18.0 | cm3/10min |
| 250°C/5.0kg | ISO1133 | 50.0 | cm3/10min | |
| 265°C/5.0kg | ISO1133 | 75.0 | cm3/10min | |
| Shrinkage rate | MD1 | 内部方法 | 0.30到0.80 | % |
| MD:3.20mm | 内部方法 | 0.40到0.60 | % | |
| TD2 | 内部方法 | 0.50到0.90 | % | |
| Water absorption rate | Saturation,23°C | ISO62 | 0.15 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.10 | % | |
| Density/specific gravity | ASTMD792,ISO1183 | 1.31 | g/cm³ | |
| Melt mass flow rate | 200°C/3.8kg | ASTMD1238 | 18 | g/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| --3 | ASTMD638 | 4600 | Mpa | |
| -- | ISO527-2/1 | 4700 | Mpa | |
| Surrender 4 | ASTMD638 | 90.0 | Mpa | |
| yield | ISO527-2/5 | 95.0 | Mpa | |
| Fracture 5 | ASTMD638 | 90.0 | Mpa | |
| crack | ISO527-2/5 | 95.0 | Mpa | |
| Surrender 6 | ASTMD638 | 3.0 | % | |
| yield | ISO527-2/5 | 3.0 | % | |
| Fracture 7 | ASTMD638 | 3.0 | % | |
| crack | ISO527-2/5 | 3.0 | % | |
| 50.0mm span 8 | ASTMD790 | 3600 | Mpa | |
| --9 | ISO178 | 4000 | Mpa | |
| --10 | ISO178 | 140 | Mpa | |
| --11 | ISO178 | 130 | Mpa | |
| Yield, 50.0mm span 12 | ASTMD790 | 126 | Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | 内部方法 | 54.0 | mg |
| Fracture bending strain 13 | ISO178 | 5.0 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 1.8MPa, unannealed, 64.0mm span 24 | ISO75-2/Af | 115 | °C | |
| -- | ASTMD1525,ISO306/B50,ISO306/B12025 | 145 | °C | |
| ASTMD1525,ISO306/A501426 | 205 | °C | ||
| BallPressure Test | 125°C | IEC60695-10-2 | Pass | |
| Flow: -40 to 40 ° C | ASTME831 | 4E-05 | cm/cm/°C | |
| ISO11359-2 | 3.7E-05 | cm/cm/°C | ||
| Flow: 23 to 80 ° C | ISO11359-2 | 4E-05 | cm/cm/°C | |
| Flow: 23 to 150 ° C | ISO11359-2 | 3.9E-05 | cm/cm/°C | |
| Horizontal: -40 to 40 ° C | ASTME831 | 9E-05 | cm/cm/°C | |
| ISO11359-2 | 7E-05 | cm/cm/°C | ||
| 0.45MPa, unannealed, 3.20mm | ASTMD648 | 175 | °C | |
| 0.45MPa, unannealed, 64.0mm span 23 | ISO75-2/Bf | 135 | °C | |
| 1.8MPa, unannealed, 3.20mm | ASTMD648 | 115 | °C | |
| Horizontal: 23 to 80 ° C | ISO11359-2 | 9E-05 | cm/cm/°C | |
| Horizontal: 23 to 150 ° C | ISO11359-2 | 1.5E-04 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | ASTMD257,IEC60093 | >1.0E+15 | ohms·cm | |
| 0.800mm,inOil | ASTMD149 | 29 | KV/mm | |
| 1.60mm,inOil | ASTMD149 | 25 | KV/mm | |
| 3.20mm, inoil | ASTMD149 | 18 | KV/mm | |
| 0.800mm, in oil | IEC60243-1 | 29 | KV/mm | |
| 1.60mm, in oil | IEC60243-1 | 25 | KV/mm | |
| 3.20mm, in oil | IEC60243-1 | 18 | KV/mm | |
| High arc combustion index | HAI | UL746 | PLC0 | |
| Hot wire ignition | HWI | UL746 | PLC0 | |
| 1MHz | ASTMD150,IEC60250 | 3.10 | ||
| 50Hz | IEC60250 | 3.00 | ||
| 60Hz | IEC60250 | 3.00 | ||
| 100Hz | IEC60250 | 3.20 | ||
| 1MHz | ASTMD150,IEC60250 | 0.014 | ||
| 50Hz | IEC60250 | 9E-03 | ||
| 60Hz | IEC60250 | 9E-03 | ||
| 100Hz | IEC60250 | 0.016 | ||
| Leakage Trace Index | -- | IEC60112 | 200 | V |
| SolutionB | IEC60112 | 100 | V |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt viscosity | 260°C,1500sec^-1 | ISO11443 | 145 | Pa·s |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| 0°C19 | ISO180/1A | 5.0 | kJ/m² | |
| 23°C20 | ISO180/1A | 6.0 | kJ/m² | |
| -30°C | ASTMD4812 | 470 | J/m | |
| 23°C | ASTMD4812 | 480 | J/m | |
| -30°C21 | ISO180/1U | 30 | kJ/m² | |
| 23°C22 | ISO180/1U | 40 | kJ/m² | |
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 37.0 | J |
| -30°C14 | ISO179/1eA | 4.0 | kJ/m² | |
| -30°C | ISO179/2C | 6.0 | kJ/m² | |
| 23°C15 | ISO179/1eA | 4.0 | kJ/m² | |
| 23°C | ISO179/2C | 6.0 | kJ/m² | |
| -30°C16 | ISO179/1eU | 30 | kJ/m² | |
| -30°C | ISO179/2U | 40 | kJ/m² | |
| 23°C17 | ISO179/1eU,ISO179/2U | 40 | kJ/m² | |
| -30°C | ASTMD256 | 47 | J/m | |
| 0°C | ASTMD256 | 47 | J/m | |
| 23°C | ASTMD256 | 47 | J/m | |
| -30°C18 | ISO180/1A | 5.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | R-Sale | ISO2039-2 | 122 | |
| Ball pressure hardness | H358/30 | ISO2039-1 | 165 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.60mm,TestingbySABIC | UL94 | HB | |
| Burning wire flammability index | 1.00mm | IEC60695-2-12 | 750 | °C |
| 3.00mm | IEC60695-2-12 | 850 | °C | |
| Extreme Oxygen Index | ISO4589-2 | 21 | % |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Filling material | ASTMD229 | 10 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.