PBT NOVADURAN™ 5010N6-X3 MITSUBISHI ENGINEERING JAPAN
83
- Unit Price:
- $5604 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant
- Application Areas:Fitness equipment Automotive Applications
- Color:--
- Grade:Halogen-free flame retardant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Across Flow : 2.00 mm | 内部方法 | 1.8 | % |
| 流量 : 2.00 mm | 内部方法 | 1.9 | % | |
| Water absorption rate | Saturation, 23°C | ISO 62 | 0.080 | % |
| Molten Volume Flow Rate (MVR) | 250°C/2.16 kg | ISO 1133 | 20.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Bending modulus 3 | ISO 178 | 2500 | Mpa | |
| Bending stress 3 | ISO 178 | 90.0 | Mpa | |
| Tensile stress | Yield | ISO 527-2/50 | 57.0 | Mpa |
| Tensile strain | Yield | ISO 527-2/50 | 4.3 | % |
| Break | ISO 527-2/50 | 20 | % | |
| Tensile modulus | ISO 527-2/1 | 2800 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Annealed | ISO 75-2/B | 165 | °C |
| 1.8 MPa, Annealed | ISO 75-2/A | 77.0 | °C | |
| Linear coefficient of thermal expansion | Flow : -30 to 35°C | ISO 11359-2 | 8.0E-5 | cm/cm/°C |
| Flow : -30 to 120°C | ISO 11359-2 | 1.2E-4 | cm/cm/°C | |
| Flow : 35 to 120°C | ISO 11359-2 | 1.4E-4 | cm/cm/°C | |
| Across Flow : -30 to 35°C | ISO 11359-2 | 8.8E-5 | cm/cm/°C | |
| Across Flow : -30 to 120°C | ISO 11359-2 | 1.2E-4 | cm/cm/°C | |
| Across Flow : 35 to 120°C | ISO 11359-2 | 1.5E-4 | cm/cm/°C | |
| Melting temperature | ISO 11357-3 | 224 | °C | |
| RTI | 0.71 mm | UL 746 | 140 | °C |
| RTI Imp | 0.71 mm | UL 746 | 120 | °C |
| RTI Elec | 0.71 mm | UL 746 | 140 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dissipation factor | 1 MHz | IEC 60250 | 0.020 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 1 | ||
| Dielectric strength | 1.00 mm | IEC 60243-1 | 21 | KV/mm |
| 2.00 mm | IEC 60243-1 | 18 | KV/mm | |
| Surface resistivity | IEC 60093 | 1.0E+15 | ohms | |
| Dielectric constant | 1 MHz | IEC 60250 | 3.20 | |
| Volume resistivity | IEC 60093 | 1.0E+16 | ohms·cm |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Injection pressure | 20.0 到 150 | Mpa | ||
| Injection speed | 中等偏快 | |||
| Drying Temperature - Vacuum Drying Machine | 120 | °C | ||
| Drying time - vacuum dryer | 5.0 到 8.0 | hr | ||
| Mold temperature | 60 到 80 | °C | ||
| Temperature at the rear of the barrel | 235 | °C | ||
| Temperature in the middle of the barrel | 240 | °C | ||
| Temperature at the front of the material cylinder | 250 | °C | ||
| Spray nozzle temperature | 245 | °C | ||
| Screw speed | 80 到 120 | rpm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 120 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.71 mm | UL 94 | V-0 | |
| 1.5 mm | UL 94 | V-0 | ||
| 3.0 mm | UL 94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.