PC IUPILON™ GS2010MPH 9001 MITSUBISHI ENGINEERING JAPAN
83
Unit Price:$2548 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:enhance Filler: Glass fiber reinf 10% filler by weight
- Application Areas:Fiber grade
- Color:--
- Grade:Blow molding grade
Technical Data Sheet
Compare
| Physical properties | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.26 | ||
| Molding shrinkage rate | ASTM D955 | 0.3 - 0.5 | % |
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 300°C/1.2kg | ISO1133 | 10 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 9.00 | cm3/10min |
| Shrinkage rate | TD:3.20mm | 0.40to0.60 | % | |
| MD:3.20mm | 0.30to0.50 | % | ||
| Water absorption rate | Saturation,23°C | ISO62 | 0.14 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2 | 4500 | Mpa | |
| Tensile stress | Break | ISO527-2 | 78.0 | Mpa |
| Tensile strain | Break | ISO527-2 | 2.9 | % |
| Bending modulus | ISO178 | 4000 | Mpa | |
| Bending stress | ISO178 | 135 | Mpa | |
| Tensile modulus | ASTM D638/ISO 527 | 2900 | kg/cm²(MPa)[Lb/in²] | |
| Bending modulus | ASTM D790/ISO 178 | 2700 | kg/cm²(MPa)[Lb/in²] | |
| bending strength | ASTM D790/ISO 178 | 90 | kg/cm²(MPa)[Lb/in²] | |
| Tensile elongation at break (elongation at break) | ASTM D638/ISO 527 | 10 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear expansion coefficient | ASTM D696/ISO 11359 | 5.8.E-05 | mm/mm.℃ | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 145 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 140 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 4E-05 | cm/cm/°C |
| TD | ISO11359-2 | 6.7E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Compared to the anti leakage trace index | CTI | UL746 | PLC4 |
| Processing performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dry conditions | 热风干燥 120℃---約4-8小时 | |||
| Processing temperature | 270-290 | °C | ||
| 290-310 | °C | |||
| 280-300 | °C | |||
| Screw speed | 50-100 | rpm | ||
| Mold temperature | 80-120 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 55 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| FlameRating | 0.75mm | UL94 | V-0 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.