PC LEXAN™ HF500R-73243 SABIC INNOVATIVE US
60
Unit Price:$2409 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 20MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:enhance Glass fiber reinforced Filler: Glass fiber reinf 9.0% filler by weight
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 16.0 | cm3/10min |
| Shrinkage rate | MD1 | 内部方法 | 0.20到0.60 | % |
| Water absorption rate | Saturation,23°C | ISO62 | 0.31 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.13 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2/1 | 3300 | Mpa | |
| Tensile stress | Yield | ISO527-2/5 | 60.0 | Mpa |
| Break | ISO527-2/5 | 45.0 | Mpa | |
| Tensile strain | Yield | ISO527-2/5 | 5.0 | % |
| Break | ISO527-2/5 | 7.0 | % | |
| Bending modulus 2 | ISO178 | 3400 | Mpa | |
| Bending stress 3 | ISO178 | 95.0 | Mpa | |
| Taber abraser | 1000Cycles,1000g,CS-17Wheel | 内部方法 | 11.0 | mg |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| -- | ISO306/B50 | 141 | °C | |
| ISO306/B120 | 143 | °C | ||
| BallPressure Test | 125°C | IEC60695-10-2 | Pass | |
| Linear coefficient of thermal expansion | MD：23to80°C | ISO11359-2 | 4E-05 | cm/cm/°C |
| thermal conductivity | ISO8302 | 0.21 | W/m/K | |
| RTIElec | UL746 | 130 | °C | |
| Evolution Calendar intelligent importer | UL746 | 125 | °C | |
| RTI | UL746 | 125 | °C | |
| 0.45MPa, unannealed, 100mm span | ISO75-2/Be | 140 | °C | |
| 1.8MPa, unannealed, 100mm span | ISO75-2/Ae | 132 | °C | |
| -- | ISO306/A50 | 147 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | >1.0E+15 | ohms | |
| Volume resistivity | IEC60093 | >1.0E+15 | ohms·cm | |
| Dielectric strength | 0.800mm,in Oil | IEC60243-1 | 33 | KV/mm |
| 1.60mm,in Oil | IEC60243-1 | 25 | KV/mm | |
| 3.20mm,in Oil | IEC60243-1 | 16 | KV/mm | |
| Relative permittivity | 50Hz | IEC60250 | 2.90 | |
| 60Hz | IEC60250 | 2.90 | ||
| 1MHz | IEC60250 | 2.80 | ||
| Dissipation factor | 50Hz | IEC60250 | 1E-03 | |
| 60Hz | IEC60250 | 1E-03 | ||
| 1MHz | IEC60250 | 0.010 | ||
| Leakage Trace Index | IEC60112 | 175 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam gap 4 | 23°C | ISO179/1eA | 8.0 | kJ/m² |
| Simply supported beam without notch impact strength 5 | -30°C | ISO179/1eU | 无断裂 | |
| 23°C | ISO179/1eU | 无断裂 | ||
| Suspended wall beam notch impact strength 6 | -30°C | ISO180/1A | 7.0 | kJ/m² |
| 23°C | ISO180/1A | 8.0 | kJ/m² | |
| Unscented Izod Impact Strength 7 | -30°C | ISO180/1U | 110 | kJ/m² |
| 23°C | ISO180/1U | 无断裂 | ||
| Impact strength of simply supported beam gap 4 | -30°C | ISO179/1eA | 7.0 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | H358/30 | ISO2039-1 | 115 | Mpa |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 1.50mm | UL94 | V-0 | |
| Burning wire flammability index | 1.00mm | IEC60695-2-12 | 960 | °C |
| Extreme Oxygen Index | ISO4589-2 | 35 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.