PC/ABS CYCOLAC™ CX7240-7M7D037 SABIC INNOVATIVE US
93
Unit Price:$3864 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant｜High impact resistance｜High mobility
- Application Areas:Electrical field｜Electronic field｜Architectural application｜Outdoor applications｜Engine hood parts｜Medical supplies｜Nursing supplies｜Plastic bag｜Casters｜Aerospace Applications｜Liquid handling
- Color:--
- Grade:--
Technical Data Sheet
Compare
| Physical | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Melt Mass-Flow Rate | 260°C/2.16 kg | ASTM D1238 | 18 g/10 min |
| Melt Volume flow Rate | 260°C/2.16 kg | ISO 1133 | 15.0 cm3/10min |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 0.40 到 0.60 % |
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.20 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.10 % |
| Thermal Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 100 °C |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 89.0 °C | |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 99.0 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 10 | ISO 75-2/Af | 93.0 °C | |
| Vicat Softening Temperature | -- | ASTM D152511, ISO 306/B5011 | 110 °C |
| -- | ISO 306/B120 | 113 °C | |
| Ball PressureTest | 73 到 77°C | IEC 60695-10-2 | 通过 |
| Linear thermal expansion coefficient | 流动 : -40 到 40°C | ASTM E831, ISO 11359-2 | 7.5E-5 cm/cm/°C |
| 横向 : -40 到 40°C | ASTM E831 | 7.5E-5 cm/cm/°C | |
| 横向 : -40°C | ISO 11359-2 | 7.5E-5 cm/cm/°C | |
| Thermal Conductivity | ISO 8302 | 0.20 W/m/K | |
| RTI Elec | UL 746 | 90.0 °C | |
| RTI Imp | UL 746 | 90.0 °C | |
| RTI | UL 746 | 90.0 °C |
| Flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| UL flame retardant rating | 0.60 mm | UL 94 | V-1 |
| 0.75 mm | UL 94 | V-0 | |
| 1.5 mm | UL 94 | 5VB | |
| 3.0 mm | UL 94 | 5VA | |
| Glow Wire Flammability Index | 0.75 mm | IEC 60695-2-12 | 960 °C |
| 0.75 mm 13 | IEC 60695-2-12 | 960 °C | |
| Glow Wire Ignition Temperature | 0.75 mm 13 | IEC 60695-2-13 | 775 °C |
| 1.0 mm | IEC 60695-2-13 | 825 °C | |
| 1.5 mm 13 | IEC 60695-2-13 | 775 °C | |
| 3.0 mm | IEC 60695-2-13 | 800 °C | |
| 3.0 mm 13 | IEC 60695-2-13 | 775 °C | |
| Oxygen Index | ISO 4589-2 | 34 % |
| Mechanical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile Modulus | -- 2 | ASTM D638 | 2600 Mpa |
| -- | ISO 527-2/1 | 2600 Mpa | |
| Tensile Strength | 屈服 3 | ASTM D638 | 65.0 Mpa |
| 屈服 | ISO 527-2/50 | 65.0 Mpa | |
| 断裂 3 | ASTM D638 | 58.0 Mpa | |
| 断裂 | ISO 527-2/50 | 50.0 Mpa | |
| Tensile Elongation | 屈服 3 | ASTM D638 | 4.1 % |
| 屈服 | ISO 527-2/50 | 4.0 % | |
| 断裂 3 | ASTM D638 | 100 % | |
| 断裂 | ISO 527-2/50 | 90 % | |
| Flexural Modulus | 50.0 mm 跨距 4 | ASTM D790 | 2500 Mpa |
| -- 5 | ISO 178 | 2500 Mpa | |
| Flexural Stress | -- 5, 6 | ISO 178 | 96.0 Mpa |
| 屈服, 50.0 mm 跨距 4 | ASTM D790 | 104 Mpa |
| Electrical Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms | |
| Volume Resistivity | IEC 60093 | > 1.0E+15 ohms·cm | |
| Dielectric Strength | 0.800 mm, 在油中 | IEC 60243-1 | 35 KV/mm |
| 1.60 mm, 在油中 | IEC 60243-1 | 25 KV/mm | |
| 3.20 mm, 在油中 | IEC 60243-1 | 17 KV/mm | |
| Comparative Tracking Index | UL 746 | PLC 3 | |
| High Amp Arc Ignition | UL 746 | PLC 0 | |
| Hot-wire Ignition | UL 746 | PLC 3 |
| Injection | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Drying Temperature | 80 到 90 °C | ||
| Drying Time | 2.0 到 4.0 hr | ||
| Suggested Max Moisture | 0.020 % | ||
| Hopper Temperature | 60 到 80 °C | ||
| Rear Temperature | 230 到 280 °C | ||
| Middle Temperature | 240 到 290 °C | ||
| Front Temperature | 250 到 300 °C | ||
| Nozzle Temperature | 250 到 300 °C | ||
| Processing (Melt) Temp | 250 到 300 °C | ||
| Mold Temperature | 60 到 85 °C | ||
| Vent Depth | 0.030 到 0.075 mm |
| Impact Properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Instrumented Dart Impact | 23°C, Total Energy | ASTM D3763 | 65.0 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.