Material Description

Technical Data Sheet

Material Description

Material Properties:Thermal stability high strength Oil resistant
Application Areas:Helmet Gear Automotive Applications
Color:--
Grade:Injection grade

Technical Data Sheet Compare

physical property	Test Condition	Test Method	Test Result	Unit
Shrinkage rate	MD：3.18mm		0.30	%
Water absorption rate	24hr	ASTMD570	1.1	%
	Water absorption rate	23°C,24hr	ISO62	1.1	%
		Water absorption rate	Saturation	ASTMD570	6.4	%
			Water absorption rate	Saturation,23°C	ISO62	6.4	%
				Water absorption rate	Equilibrium,50%RH	ASTMD570	1.8	%
				Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO62	1.8	%
Density/specific gravity		ASTMD792	1.39	g/cm³
Density/specific gravity	Density/specific gravity		ISO1183	1.39	g/cm³

Mechanical performance	Test Condition	Test Method	Test Result	Unit
Tensile strength	Break,-40°C	ASTMD638	283	Mpa
	Tensile strength	Break,23°C	ASTMD638	195	Mpa
		Tensile strength	Break,80°C	ASTMD638	110	Mpa
		Tensile strength	Tensile strength	Break,121°C	ASTMD638	83.0	Mpa
Bending stress	23°C	ISO178	260	Mpa
Tensile stress	Break,23°C	ISO527-2	185	Mpa
	Tensile stress	Break,80°C	ISO527-2	110	Mpa
		Tensile stress	Break,120°C	ISO527-2	83.0	Mpa
			Tensile stress	Break,150°C	ISO527-2	80.0	Mpa
			Tensile stress	Tensile stress	Break,-40°C	ISO527-2	283	Mpa
Tensile strain	Break,-40°C	ISO527-2	3.6	%
	Tensile strain	Break,23°C	ISO527-2	3.5	%
		Tensile strain	Break,80°C	ISO527-2	7.0	%
			Tensile strain	Break,120°C	ISO527-2	7.0	%
			Tensile strain	Tensile strain	Break,150°C	ISO527-2	6.0	%
Tensile modulus	-40°C	ISO527-2	10500	Mpa
	Tensile modulus	23°C	ISO527-2	10100	Mpa
		Tensile modulus	80°C	ISO527-2	4430	Mpa
			Tensile modulus	120°C	ISO527-2	3550	Mpa
			Tensile modulus	Tensile modulus	150°C	ISO527-2	3440	Mpa
elongation	Break,-40°C	ASTMD638	3.6	%
	elongation	Break,23°C	ASTMD638	3.5	%
		elongation	Break,80°C	ASTMD638	7.0	%
		elongation	elongation	Break,121°C	ASTMD638	7.0	%
Bending modulus	-40°C	ASTMD790	9830	Mpa
	Bending modulus	23°C	ASTMD790	9040	Mpa
		Bending modulus	65°C	ASTMD790	4020	Mpa
			Bending modulus	90°C	ASTMD790	3750	Mpa
				Bending modulus	121°C	ASTMD790	3320	Mpa
				Bending modulus	Bending modulus	23°C	ISO178	8200	Mpa
bending strength	-40°C	ASTMD790	380	Mpa
	bending strength	23°C	ASTMD790	297	Mpa
		bending strength	65°C	ASTMD790	160	Mpa
			bending strength	90°C	ASTMD790	140	Mpa
			bending strength	bending strength	121°C	ASTMD790	112	Mpa

Thermal performance	Test Condition	Test Method	Test Result	Unit
Hot deformation temperature	0.45MPa,Unannealed	ASTMD648	218	°C
	Hot deformation temperature	0.45MPa,Unannealed	ISO75-2/B	215	°C
		Hot deformation temperature	1.8MPa,Unannealed	ASTMD648	210	°C
		Hot deformation temperature	Hot deformation temperature	1.8MPa,Unannealed	ISO75-2/A	205	°C
Melting temperature (DSC)		ISO3146	220	°C
Linear coefficient of thermal expansion	MD	ASTME831	3.8E-05	cm/cm/°C
	Linear coefficient of thermal expansion	MD		2.1E-05	cm/cm/°C
	Linear coefficient of thermal expansion	Linear coefficient of thermal expansion	TD		7E-05	cm/cm/°C
RTIElec	0.71mm	UL746	130	°C
	RTIElec	1.5mm	UL746	140	°C
	RTIElec	RTIElec	3.0mm	UL746	140	°C
Evolution Calendar intelligent importer	0.71mm	UL746	115	°C
	Evolution Calendar intelligent importer	1.5mm	UL746	115	°C
	Evolution Calendar intelligent importer	Evolution Calendar intelligent importer	3.0mm	UL746	120	°C
RTIStr	0.71mm	UL746	130	°C
	RTIStr	1.5mm	UL746	140	°C
	RTIStr	RTIStr	3.0mm	UL746	140	°C
Peak melting temperature		ASTMD3418	220	°C

Electrical performance	Test Condition	Test Method	Test Result	Unit
VolumeResistivity	1.50mm	ASTMD257	>1.0E+13	ohms·cm
Dissipation factor	100Hz	IEC60250	0.020
Dissipation factor	Dissipation factor	1MHz	IEC60250	0.020
Dielectric strength		IEC60243-1	44	KV/mm
Dielectric constant	100Hz	IEC60250	4.20
Dielectric constant	Dielectric constant	1MHz	IEC60250	3.60
Volume resistivity		IEC60093	>1.0E+13	ohms·cm

Impact performance	Test Condition	Test Method	Test Result	Unit
Impact strength of simply supported beam without notch	23°C	ISO179	88	kJ/m²
Falling impact resistance	23°C	内部方法	4.07	J
Charpy Notched Impact Strength	-30°C	ISO179	10	kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength	23°C	ISO179	15	kJ/m²
Impact strength of cantilever beam gap	-40°C	ASTMD256	110	J/m
	Impact strength of cantilever beam gap	23°C	ASTMD256	150	J/m
		Impact strength of cantilever beam gap	-40°C	ISO180	8.5	kJ/m²
		Impact strength of cantilever beam gap	Impact strength of cantilever beam gap	23°C	ISO180	10	kJ/m²

hardness	Test Condition	Test Method	Test Result	Unit
Rockwell hardness	R-Scale	ASTMD785	121

flammability	Test Condition	Test Method	Test Result	Unit
UL flame retardant rating	0.60mm	UL94	HB
	UL flame retardant rating	0.71mm	UL94	HB
		UL flame retardant rating	1.5mm	UL94	HB
		UL flame retardant rating	UL flame retardant rating	3.0mm	UL94	HB

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.