PC LNP™ THERMOCOMP™ DX14354X-GN5H004 SABIC INNOVATIVE NANSHA
82
- Unit Price:
- $7022 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40to0.80 | % |
| Water absorption rate | 饱和,23°C | ISO62 | 0.40 | % |
| 平衡,23°C,50%RH | ISO62 | 0.15 | % | |
| Melt mass flow rate | 300°C/1.2kg | ASTMD1238 | 16 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 15.1 | cm3/10min |
| density | ASTMD792 | 1.19 | g/cm³ | |
| ISO1183 | 1.19 | g/cm³ |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile strength | 断裂 | ASTMD638 | 59.0 | Mpa |
| 屈服 | ASTMD638 | 58.0 | Mpa | |
| Tensile stress | 断裂 | ISO527-2/50 | 57.0 | Mpa |
| 屈服 | ISO527-2/50 | 56.0 | Mpa | |
| Tensile strain | 断裂 | ISO527-2/50 | 110 | % |
| 屈服 | ISO527-2/50 | 6.0 | % | |
| Tensile modulus | ASTMD638 | 2100 | Mpa | |
| ISO527-2/1 | 2000 | Mpa | ||
| elongation | 屈服 | ASTMD638 | 6.0 | % |
| 断裂 | ASTMD638 | 120 | % | |
| Bending modulus | 50.0mm跨距 | ASTMD790 | 2400 | Mpa |
| ISO178 | 2100 | Mpa | ||
| bending strength | ISO178 | 87.0 | Mpa | |
| 屈服,50.0mm跨距 | ASTMD790 | 92.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 118 | °C |
| 1.8MPa,未退火,3.20mm | ASTMD648 | 123 | °C | |
| RTIElec | UL746 | 125 | °C | |
| Evolution Calendar intelligent importer | UL746 | 115 | °C | |
| RTIStr | UL746 | 120 | °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ASTME831 | 6.1E-05 | cm/cm/°C |
| MD：-40到40°C | ISO11359-2 | 6.1E-05 | cm/cm/°C | |
| TD：-40到40°C | ASTME831 | 6.2E-05 | cm/cm/°C | |
| TD：-40到40°C | ISO11359-2 | 6.2E-05 | cm/cm/°C | |
| Vicat softening temperature | ASTMD152510 | 140 | °C | |
| -- | ISO306/B50 | 139 | °C | |
| -- | ISO306/B120 | 141 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 67.0 | J |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 35 | kJ/m² |
| 23°C | ISO179/1eA | 70 | kJ/m² | |
| Impact strength of cantilever beam gap | -30°C | ASTMD256 | 660 | J/m |
| 23°C | ASTMD256 | 790 | J/m | |
| -30°C | ISO180/1A | 30 | kJ/m² | |
| 23°C | ISO180/1A | 65 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Burning wire flammability index | 1.6mm | IEC60695-2-12 | 960 | °C |
| Hot filament ignition temperature | 1.5mm | IEC60695-2-13 | 825 | °C |
| 3.0mm | IEC60695-2-13 | 825 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.