Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|
| Molten Volume Flow Rate (MVR) | 240°C/5.0 kg | ISO 1133 | 26.0 | cm3/10min |
| Shrinkage rate - lateral flow rate | 2.00 mm 3 | ISO 294-4 | 0.40 到 0.60 | % |
| Shrinkage rate - lateral flow rate | 3.00 mm 4 | ISO 2577 | 0.40 到 0.60 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Tensile modulus | 23°C | ISO 527-2/1 | 2650 | Mpa |
| Tensile stress | Yield, 23°C | ISO 527-2/50 | 61.0 | Mpa |
| Tensile stress | Break, 23°C | ISO 527-2/50 | 44.0 | Mpa |
| Tensile strain | Yield, 23°C | ISO 527-2/50 | 4.0 | % |
| Tensile strain | Break, 23°C | ISO 527-2/50 | 30 | % |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Linear coefficient of thermal expansion | Flow : 23 to 55°C | ISO 11359-2 | 7.5E-5 | cm/cm/°C |
| Linear coefficient of thermal expansion | Across Flow : 23 to 55°C | ISO 11359-2 | 7.6E-5 | cm/cm/°C |
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 86.0 | °C |
| Hot deformation temperature | 1.8 MPa, Unannealed | ISO 75-2/A | 78.0 | °C |
| Vicat softening temperature | -- | ISO 306/B50 | 89.0 | °C |
| Vicat softening temperature | -- | ISO 306/B120 | 95.0 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Surface resistivity | | IEC 60093 | 5.0E+17 | ohms |
| Volume resistivity | 23°C | IEC 60093 | 2.0E+18 | ohms·cm |
| Filling analysis | Test Condition | Test Method | Test Result | Unit |
|---|
| Melt Viscosity | 240°C | ISO 11443-A | 155 | Pa·s |
| ISO 9660 | | | PC+ABS-FR(40) | |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|
| Drying Temperature - Dry Air Dryer | | | 80 | °C |
| Drying time - Dry Air Dryer | | | 4.0 | hr |
| Suggested maximum moisture content | | | < 0.020 | % |
| Processing (melt) temperature | | | 240 到 270 | °C |
| Mold temperature | | | 60 到 90 | °C |
| Suggested injection volume | | | 30 到 70 | % |
| Temperature at the rear of the barrel | | | 220 到 230 | °C |
| Temperature in the middle of the barrel | | | 225 到 235 | °C |
| Temperature at the front of the material cylinder | | | 230 到 240 | °C |
| Spray nozzle temperature | | | 255 到 265 | °C |
| Back pressure | | | 5.00 到 15.0 | Mpa |
| Exhaust hole depth | | | 0.025 到 0.075 | mm |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|
| Unscented Izod impact strength | 23°C | ISO 180 | 无断裂 | |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|
| Extreme Oxygen Index 5 | | ISO 4589-2 | 31 | % |
| UL flame retardant rating | 1.5 mm | UL 94 | V-0 5VB | |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.