PC Makrolon® 2407 020056 COVESTRO SHANGHAI
96
- Unit Price:
- $4924 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 24.8MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Low viscosity UV resistance High mobility Thermal stability Good demolding performanc
- Application Areas:Electrical field Electronic field Industrial applications Automotive sector currency currency
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD2.0mm | ISO294-4 | 0.65 | % |
| TD2.0mm | ISO294-4 | 0.70 | % | |
| Water absorption rate | (23°C,24hr) | ISO62 | 0.30 | % |
| (23°C,50RH) | ISO62 | 0.12 | % | |
| Density/specific gravity | ISO1183 | 1.2 | g/cm³ | |
| Melt flow index | 300℃/1.2Kg | ISO1133 | 19.0 | cm3/10min |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile creep modulus | 1Hr | ISO899-1 | 2200 | Mpa |
| 1000Hr | ISO899-1 | 1900 | Mpa | |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 65 | kJ/m² |
| -30°C | ISO179/1eA | 14 | kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO180/1A | 75 | kJ/m² |
| -30°C | ISO180/1A | 12 | kJ/m² | |
| elongation at break | 23°C | ISO527-2 | >50 | % |
| Tensile modulus | 23°C | ISO527-2 | 2400 | Mpa |
| tensile strength | 23°C | ISO527-2 | 66.0 | Mpa |
| Bending modulus | 23°C | ISO178 | 2350 | Mpa |
| bending strength | 23°C | ISO178 | 98.0 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45MPaUnannealed | ISO75-2/Bf | 136 | °C |
| 1.80MPaAnnealed | ISO75-2/Af | 124 | °C | |
| Vicat softening temperature | ISO306/B50 | 143 | °C | |
| Coefficient of linear expansion | MD | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| TD | ISO11359-2 | 6.5E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Insulation strength | IEC60243-1 | 25 | KV/mm | |
| Volume resistance | IEC60093 | 1E+15 | Ω.cm | |
| Dissipation factor | 23°C | IEC60250 | 5E-04 | 100HZ |
| 23°C | IEC60250 | 9E-03 | 1MHz | |
| 相对漏电起痕指数 | IEC60112 | 250 | V | |
| Dielectric constant | 23°C | IEC60250 | 3.00 | 1MHz |
| Surface resistance | IEC60093 | 1E+16 | Ω.cm |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Ball pressure hardness | ISO2039-1 | 116 | Mpa |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Transmittance of 1000 μ m | ISO13468-2 | 89.0 | % | |
| Refractive index | ISO489 | 1.58 | °C |
| Flame retardant performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Fire rating | 氧指数 | ISO4589-2 | 27 | % |
| UL-94 | 0.75mm | V-2 | ||
| UL-94 | 1.50mm | V-2 | ||
| UL-94 | 2.60mm | V-2 | ||
| UL-94 | 2.70mm | HB | ||
| UL-94 | 3.00mm | HB | ||
| UL-94 | 6.00mm | HB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.