LCP VECTRA® FIT72 D-2 BK210P CELANESE USA
97
- Unit Price:
- $6222 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 50MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Electrostatic discharge p Halogen-free Flame retardant enhance Glass fiber reinforced Low warpage high flowabi Filler: Glass mineral 35% filler by weight
- Application Areas:Electrical tools Home appliance components Automotive Applications
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD | ISO294-4 | 0.43 | % |
| MD | ISO294-4 | 0.050 | % | |
| TD | ISO 294-4 | 0.43 | % | |
| MD | ISO 294-4 | 0.05 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile stress | Break | ISO 527-2/1A/5 | 110 | Mpa |
| Break | ISO527-2/1A/50 | 110 | Mpa | |
| Tensile strain | Break | ISO527-2/1A/50 | 2.0 | % |
| Break | ISO 527-2/1A/5 | 2 | % | |
| Tensile modulus | ISO 527-2/1A/1 | 12000 | Mpa | |
| ISO527-2/1A/1 | 12000 | Mpa | ||
| Bending modulus | 23℃ | ISO 178 | 12000 | Mpa |
| 23°C | ISO178 | 12000 | Mpa | |
| Bending stress | 23℃ | ISO 178 | 140 | Mpa |
| 23°C | ISO178 | 140 | Mpa | |
| Impact strength of simply supported beam without notch | 23℃ | ISO 179/1eA | 30 | kJ/m² |
| Fracture bending strain | ISO178 | 2.5 | % | |
| ISO 178 | 2.5 | % | ||
| Charpy Notched Impact Strength | 23℃ | ISO 179/1eA | 8 | kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melting temperature 3 | ISO11357-3 | 331 | °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8E-06 | cm/cm/℃ |
| TD | ISO 11359-2 | 4.3E-05 | cm/cm/℃ | |
| MD | ISO11359-2 | 8E-06 | cm/cm/°C | |
| TD | ISO11359-2 | 4.3E-05 | cm/cm/°C | |
| Melting temperature | ISO 11357-3 | 331 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 284 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 240 | °C | |
| 0.45 MPa, Unannealed | ISO 75-2/B | 284 | °C | |
| 1.8 MPa, Unannealed | ISO 75-2/A | 240 | °C |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179/1eU | 30 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.