PC/ABS MULTILON® TN-7000 TEIJIN JAPAN
89
- Unit Price:
- $3568 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant
- Application Areas:OA device Computer components Electrical applications Business equipment
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Flow | 0.5-0.7 | % | |
| Across Flow | 0.5-0.7 | % | ||
| TD:4.00mm | 内部方法 | 0.50to0.70 | % | |
| MD:4.00mm | 内部方法 | 0.50to0.70 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO527-2/1 | 2600 | Mpa | |
| Tensile stress | Yield | ISO527-2/50 | 63.0 | Mpa |
| Break | ISO527-2/50 | 48.0 | Mpa | |
| Tensile strain | Yield | ISO527-2/50 | 3.0 | % |
| Break | ISO527-2/50 | 80 | % | |
| Bending modulus 2 | ISO178 | 2600 | Mpa | |
| Bending stress 2 | ISO178 | 95.0 | Mpa | |
| Tensile modulus | ISO 527-1,-2 | 2600 | Mpa | |
| Tensile yield stress | ISO 527-1,-2 | 63 | Mpa | |
| Tensile fracture stress | ISO 527-1,-2 | 48 | Mpa | |
| Tensile yield elongation | ISO 527-1,-2 | 3 | % | |
| Tensile strain at break | ISO 527-1,-2 | 80 | % | |
| Bending modulus | ISO 178 | 2600 | Mpa | |
| bending strength | ISO 178 | 95 | Mpa | |
| Izod notched impact strength | 没Notched | ISO 179 | NB | KJ/m |
| 带Notched | ISO 179 | 15 | KJ/m |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | -，1.80MPa | ISO 75-1 | 84 | °C |
| -，0.45Mpa | ISO 75-2 | 94 | °C | |
| vicat softening point | ISO 306 | 97 | °C | |
| Coefficient of linear expansion | Flow | ISO 11359-2 | 0.8 | |
| Across Flow | ISO 11359-2 | 0.8 | ||
| Flame retardancy | UL94 | V-0 | ||
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 94.0 | °C |
| 1.8MPa,Unannealed | ISO75-2/A | 84.0 | °C | |
| Vicat softening temperature | ISO306/B50 | 97.0 | °C | |
| Linear coefficient of thermal expansion | MD | ISO11359-2 | 8E-05 | cm/cm/°C |
| TD | ISO11359-2 | 8E-05 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC60093 | 1E+16 | ohms |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO179 | NoBreak |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.70mm | UL94 | V-2 | |
| 1.2mm | UL94 | V-1 | ||
| 1.5mm | UL94 | V-0 | ||
| 2.0mm | UL94 | 5VB |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.