LCP LAPEROS® A130 A430 BK010P JAPAN POLYPLASTIC
120
Unit Price:$6190 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 50MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Flame retardant Glass fiber reinforced Thermal stability Chemical resistance
- Application Areas:Electrical field Electronic field Household appliances Household appliances
- Color:--
- Grade:Injection grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | Across Flow | ISO 294-4 | 0.40 | % |
| 流量 | ISO 294-4 | 0.20 | % | |
| Water absorption rate | Equilibrium, 23°C, 50% RH | ISO 62 | 0.040 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO 527-2/1A | 15000 | Mpa | |
| Tensile stress | Break | ISO 527-2/1A/5 | 190 | Mpa |
| Tensile strain | Break | ISO 527-2/1A/5 | 2.1 | % |
| Tensile creep modulus | 1 hr | ISO 899-1 | 12600 | Mpa |
| 1000 hr | ISO 899-1 | 10900 | Mpa | |
| Bending modulus | 23°C | ISO 178 | 14500 | Mpa |
| Bending stress | 23°C | ISO 178 | 280 | Mpa |
| Compressive modulus | ISO 604 | 14500 | Mpa | |
| Compressive stress | 1% Strain | ISO 604 | 100 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 250 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 235 | °C | |
| 8.0 MPa, Unannealed | ISO 75-2/C | 190 | °C | |
| Vicat softening temperature | ISO 306/B50 | 160 | °C | |
| Melting temperature 3 | ISO 11357-3 | 280 | °C | |
| Linear coefficient of thermal expansion | Flow | ISO 11359-2 | 6.0E-6 | cm/cm/°C |
| Across Flow | ISO 11359-2 | 2.3E-5 | cm/cm/°C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Surface resistivity | IEC 60093 | > 1.0E+15 | ohms | |
| Volume resistivity | IEC 60093 | 1.0E+15 | ohms·cm | |
| Dielectric strength | IEC 60243-1 | 31 | KV/mm | |
| Relative permittivity | 100 Hz | IEC 60250 | 4.20 | |
| 1 MHz | IEC 60250 | 3.70 | ||
| Dissipation factor | 100 Hz | IEC 60250 | 0.016 | |
| 1 MHz | IEC 60250 | 0.018 | ||
| Arc resistance | 内部方法 | 140 | sec | |
| Leakage Trace Index | IEC 60112 | 175 | V |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 150 | °C | ||
| drying time | 4.0 到 6.0 | hr | ||
| Suggested maximum moisture content | 0.010 | % | ||
| Hopper temperature | 20 到 30 | °C | ||
| Temperature at the rear of the barrel | 270 到 280 | °C | ||
| Temperature in the middle of the barrel | 275 到 285 | °C | ||
| Temperature at the front of the material cylinder | 280 到 290 | °C | ||
| Spray nozzle temperature | 290 到 300 | °C | ||
| Processing (melt) temperature | 285 到 295 | °C | ||
| Mold temperature | 80 到 120 | °C | ||
| Injection speed | 快速 | |||
| Back pressure | < 3.00 | Mpa |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unscented Izod impact strength | 23°C | ISO 180/1U | 29 | kJ/m² |
| hardness | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Rockwell hardness | M -Sale | ISO 2039-2 | 85 |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | UL 94 | V-0 | ||
| Extreme Oxygen Index | ISO 4589-2 | 45 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.