POP AFFINITY™ PL 1850G DOW THAILAND
155
- Unit Price:
- $2469 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 22.5MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:--
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Melt mass flow rate | 190°C/2.16kg | ASTMD1238 | 3.0 | g/10min |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Vicat softening temperature | ASTMD1525 | 85.0 | °C | |
| Melting temperature (DSC) | 内部方法 | 98.0 | °C |
| film | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Film thickness - tested | 20 | µm | ||
| Membrane puncture strength | 20µm | 内部方法 | 4.28 | J |
| Membrane piercing force | 20µm | 内部方法 | 47.6 | N |
| Membrane puncture resistance | 20µm | 内部方法 | 31.4 | J/cm³ |
| Secant modulus | 2%Secant,MD:20μm | ASTMD882 | 108 | Mpa |
| Initial sealing temperature 3 | 20µm | 内部方法 | 93.9 | °C |
| Secant modulus | 2%Secant,TD:20μm | ASTMD882 | 115 | Mpa |
| Tensile strength | MD:Yield,20μm | ASTMD882 | 9.93 | Mpa |
| TD:Yield,20μm | ASTMD882 | 5.45 | Mpa | |
| MD:Break,20μm | ASTMD882 | 44.6 | Mpa | |
| TD:Break,20μm | ASTMD882 | 29.8 | Mpa | |
| elongation | MD:Break,20μm | ASTMD882 | 350 | % |
| TD:Break,20μm | ASTMD882 | 570 | % | |
| Falling hammer impact | 20µm | ASTMD1709B | >830 | g |
| Elmondov tear strength 2 | MD:20µm | ASTMD1922 | 120 | g |
| TD:20µm | ASTMD1922 | 410 | g |
| optical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| gloss | 20°,20.3µm | ASTMD2457 | 144 | |
| Haze | 20.3µm | ASTMD1003 | 0.70 | % |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.