PA66 Vydyne® R550 NAT ASCEND USA
90
- Unit Price:
- $4958 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 25.6MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Food grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | TD:23°C,2.00mm | ISO294-4 | 0.90 | % |
| MD:23°C,2.00mm | ISO294-4 | 0.40 | % | |
| Water absorption rate | 23°C,24hr | ISO62 | 0.50 | % |
| Equilibrium,23°C,50%RH | ISO62 | 1.2 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2 | 16800 | Mpa |
| Tensile stress | Break,23°C | ISO527-2 | 240 | Mpa |
| Tensile strain | Break,23°C | ISO527-2 | 2.5 | % |
| Bending modulus | 23°C | ISO178 | 16000 | Mpa |
| Bending stress | 23°C | ISO178 | 350 | Mpa |
| Poisson's ratio | ISO527-2 | 0.40 |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 1.8MPa,Unannealed | ISO75-2/A | 255 | °C |
| Melting temperature | ISO11357-3 | 260 | °C | |
| Linear coefficient of thermal expansion | MD：23to55°C,2.00mm | ISO11359-2 | 1.2E-05 | cm/cm/°C |
| TD：23to55°C,2.00mm | ISO11359-2 | 1E-04 | cm/cm/°C | |
| RTIElec | 0.75mm | UL746 | 125 | °C |
| 1.5mm | UL746 | 125 | °C | |
| 3.0mm | UL746 | 125 | °C | |
| Evolution Calendar intelligent importer | 0.75mm | UL746 | 110 | °C |
| 1.5mm | UL746 | 110 | °C | |
| 3.0mm | UL746 | 110 | °C | |
| RTIStr | 0.75mm | UL746 | 130 | °C |
| 1.5mm | UL746 | 130 | °C | |
| 3.0mm | UL746 | 130 | °C | |
| Hot deformation temperature | 0.45MPa,Unannealed | ISO75-2/B | 260 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| VolumeResistivity | 0.750mm | IEC60093 | 1E+13 | ohms·cm |
| Dielectric strength | 1.00mm | IEC60243 | 22 | KV/mm |
| Arc resistance | 3.00mm | ASTMD495 | PLC5 | |
| Leakage Trace Index | 3.00mm | IEC60112 | 600 | V |
| High arc combustion index (HAI) | 0.75mm | UL746 | PLC0 | |
| 1.5mm | UL746 | PLC0 | ||
| 3.0mm | UL746 | PLC0 | ||
| High voltage arc tracing rate | HVTR | UL746 | PLC1 | |
| Hot wire ignition (HWI) | 0.75mm | UL746 | PLC4 | |
| 1.5mm | UL746 | PLC4 | ||
| 3.0mm | UL746 | PLC4 |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO179/1eU | 91 | kJ/m² |
| 23°C | ISO179/1eU | 95 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL94 | HB | |
| 1.5mm | UL94 | HB | ||
| 3.0mm | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Automotive Materials | thicknessd=1mm | FMVSS302 | + |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.