PA6/66 Ultramid® A3WG6 BK 00546 BASF GERMANY
86
- Unit Price:
- $4247 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:--
- Application Areas:--
- Color:--
- Grade:Enhanced level
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Apparent density | 0.70 | g/cm³ | ||
| Molten Volume Flow Rate (MVR) | 275°C/5.0 kg | ISO 1133 | 10.0 | cm3/10min |
| Shrinkage rate | Across Flow | ISO 294-4 | 1.2 | % |
| 流量 | ISO 294-4 | 0.40 | % | |
| Water absorption rate | Saturation, 23°C | ISO 62 | 5.6 到 6.3 | % |
| Equilibrium, 23°C, 50% RH | ISO 62 | 1.5 到 1.9 | % | |
| Stickiness number | 96% H2SO4 | ISO 307 | 160 | cm³/g |
| Mold Shrinkage - Constrained 2 | 0.40 到 0.50 | % |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Tensile modulus | ISO 527-2 | 9500 | Mpa | |
| Tensile stress | Break | ISO 527-2 | 185 | Mpa |
| Tensile strain | Break | ISO 527-2 | 3.7 | % |
| Bending modulus | ISO 178 | 9200 | Mpa | |
| Bending stress | ISO 178 | 285 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot deformation temperature | 0.45 MPa, Unannealed | ISO 75-2/B | 260 | °C |
| 1.8 MPa, Unannealed | ISO 75-2/A | 245 | °C | |
| Melting temperature | ISO 11357-3 | 260 | °C | |
| Polymer Abbreviation | PA66-GF30 |
| injection | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| drying temperature | 80 | °C | ||
| drying time | 4.0 | hr | ||
| Suggested maximum moisture content | 0.15 | % | ||
| Hopper temperature | 80 | °C | ||
| Temperature at the rear of the barrel | 290 | °C | ||
| Temperature in the middle of the barrel | 290 | °C | ||
| Temperature at the front of the material cylinder | 290 | °C | ||
| Spray nozzle temperature | 290 | °C | ||
| Processing (melt) temperature | 280 到 300 | °C | ||
| Mold temperature | 80 到 90 | °C | ||
| Residence Time | < 10.0 | min | ||
| Screw Speed | < 18 | m/min |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 75 | kJ/m² |
| 23°C | ISO 179/1eU | 90 | kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.