PC LEXAN™ 505RU-131 SABIC INNOVATIVE SHANGHAI
99
- Unit Price:
- $2979 USD/MT
- Packaging Specification:
- 25 KG/PKG
- Supply Quantity:
- 10MT
- Delivery Terms:
- FOB
- Port of Loading:
- China Main Port
- Accepted Payment Methods:
- T/T
- Shipping:
- Negotiate supplier for shipping details
Supplier Information
ASIA PLASTIC EXCHANGE LIMITED
+86 755 2787 3515View
serv********View
For more detailed information including pricing, customization, and shipping, please contact supplier.
Material Description
Technical Data Sheet
Material Description
- Material Properties:Bromine free flame retard High transparency
- Application Areas:Home appliance products Automotive components
- Color:--
- Grade:Wear resistant grade
Technical Data Sheet
Compare
| physical property | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.40to0.60 | % |
| Water absorption rate | Saturation,23°C | ISO62 | 0.30 | % |
| Equilibrium,23°C,50%RH | ISO62 | 0.15 | % | |
| Melt mass flow rate | 300°C/1.2kg | ASTMD1238 | 8.0 | g/10min |
| Melt volume flow rate | 300°C/1.2kg | ISO1133 | 7.00 | cm3/10min |
| Outdoor applicability | UL746C | f1 |
| Mechanical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Elongation rate 4 | Break | ASTMD638 | 6.0 | % |
| Bending modulus 5 | ISO178 | 3500 | Mpa | |
| Elongation rate 3 | Yield | ASTMD638 | 4.0 | % |
| Tensile modulus 2 | ASTMD638 | 3600 | Mpa | |
| Tensile strength 3 | Break | ASTMD638 | 62.0 | Mpa |
| Yield | ASTMD638 | 74.0 | Mpa | |
| Bending modulus 4 | 50.0mmSpan | ASTMD790 | 3200 | Mpa |
| Bending strength 4 | Yield,50.0mmSpan | ASTMD790 | 114 | Mpa |
| Tensile modulus | ISO527-2/1 | 3500 | Mpa | |
| Tensile stress | Break | ISO527-2/5 | 60.0 | Mpa |
| Yield | ISO527-2/5 | 72.0 | Mpa | |
| Tensile strain | Break | ISO527-2/5 | 6.0 | % |
| Yield | ISO527-2/5 | 3.0 | % | |
| Bending strength 5,6 | ISO178 | 122 | Mpa |
| Thermal performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Linear coefficient of thermal expansion | MD：-40to40°C | ASTME831 | 5E-05 | cm/cm/°C |
| MD：-40to40°C | ISO11359-2 | 5E-05 | cm/cm/°C | |
| TD：-40to40°C | ASTME831 | 7.4E-05 | cm/cm/°C | |
| TD：-40to40°C | ISO11359-2 | 8.5E-05 | cm/cm/°C | |
| Hot deformation temperature | 1.8MPa,Unannealed,3.20mm | ASTMD648 | 137 | °C |
| Vicat softening temperature | ASTMD152510 | 149 | °C | |
| -- | ISO306/B50 | 147 | °C | |
| -- | ISO306/B120 | 149 | °C | |
| BallPressure Test | 125°C | IEC60695-10-2 | Pass | |
| Hot deformation temperature 9 | 1.8MPa,Unannealed,64.0mmSpan | ISO75-2/Af | 136 | °C |
| Electrical performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot wire ignition | HWI | UL746 | PLC3 | |
| High arc combustion index | HAI | UL746 | PLC0 | |
| Compared to the anti leakage trace index | CTI | UL746 | PLC3 | |
| Leakage Trace Index | IEC60112 | 175 | V |
| Impact performance | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Unscented Izod Impact Strength 8 | -30°C | ISO180/1U | 73 | kJ/m² |
| 23°C | ISO180/1U | NoBreak | ||
| Dart impact equipped with measuring instruments | 23°C,TotalEnergy | ASTMD3763 | 25.0 | J |
| Impact strength of simply supported beam gap 7 | -30°C | ISO179/1eA | 7.0 | kJ/m² |
| 23°C | ISO179/1eA | 10 | kJ/m² | |
| The impact strength of a simply supported beam without a notch is 7 | -30°C | ISO179/1eU | NoBreak | |
| 23°C | ISO179/1eU | NoBreak | ||
| Suspended wall beam gap impact strength 8 | -30°C | ISO180/1A | 8.0 | kJ/m² |
| 23°C | ISO180/1A | 10 | kJ/m² |
| flammability | Test Condition | Test Method | Test Result | Unit |
|---|---|---|---|---|
| Hot filament ignition temperature | 1.0mm | IEC60695-2-13 | 850 | °C |
| 3.0mm | IEC60695-2-13 | 875 | °C | |
| UL flame retardant rating | 0.75mm,TestingbySABIC | UL94 | V-2 | |
| 1.5mm,TestingbySABIC | UL94 | V-0 | ||
| 3.0mm,TestingbySABIC | UL94 | 5VB5VA | ||
| Burning wire flammability index | 0.75mm | IEC60695-2-12 | 960 | °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.